Sample: As-received Forged Ti-7Al Alloy Ungroup Processes
Last Updated: 4 years ago Owner: Qianying Shi ID: 6775
Annealing Heat Treatment (1)
Time:
1 h
Cooling Type:
{ "name": "Water Quench", "value": "water_quench" }
Temperature:
945 C
Cooling Rate:
No value
Fractography (1)
Current:
No value
Step Size:
No value microns
Vertical Direction:
No value
Magnification:
No value
Acquisition Time:
No value
Voltage:
No value
Scan Size Width:
No value microns
Sample Tilt:
No value degress
Horizontal Direction:
No value
Scan Size Height:
No value microns
Working Distance:
No value mm
Files
Microstructure & Texture (1)
Acquisition Time:
No value
Working Distance:
No value mm
Sample Tilt:
No value degress
Magnification:
No value
Scan Size Height:
No value microns
Horizontal Direction:
No value
Voltage:
No value
Vertical Direction:
No value
Scan Size Width:
No value microns
Current:
No value
Step Size:
No value microns
Files
Receive Materials from Timet (1)
Supplier:
No value
Manufacturer:
Timet
Manufacturing Date:
No value
Production Method:
No value
Small Fatigue Crack Growth (1)
Resonating Frequency:
No value kHz
Stress Ratio:
-1
Test Environment:
Air
Power Control:
No value
Amplifiers Count:
No value
Calibration Constant:
No value
Max Stress:
No value MPa
Test Temperature:
25 C
Files
Tensile Test (1)
Temperature:
25 C
Gage Length:
10 mm
Test Rate:
10^-4/s
Force Type:
{ "name": "Screw", "value": "screw" }
Control Mode:
{ "name": "Displacement", "value": "displacement" }
Sample Geometry:
{ "name": "Cylindrical", "value": "cylindrical" }
Files
Ultrasonic Fatigue Lifetime (1)
Amplifiers Count:
No value
Stress Ratio:
-1
Test Temperature:
25 C
Max Stress:
No value MPa
Calibration Constant:
No value
Power Control:
No value
Test Environment:
Air
Resonating Frequency:
No value kHz