Sample: As-received Forged Ti-4Al Alloy Ungroup Processes
Last Updated: 4 years ago Owner: Qianying Shi ID: 6776
Annealing Heat Treatment (1)
Cooling Type:
{ "name": "Water Quench", "value": "water_quench" }
Time:
1 h
Cooling Rate:
No value
Temperature:
898 C
Fractography (1)
Working Distance:
No value mm
Voltage:
No value
Horizontal Direction:
No value
Scan Size Width:
No value microns
Sample Tilt:
No value degress
Step Size:
No value microns
Magnification:
No value
Vertical Direction:
No value
Scan Size Height:
No value microns
Acquisition Time:
No value
Current:
No value
Files
Microstructure & Texture (1)
Magnification:
No value
Horizontal Direction:
No value
Scan Size Height:
No value microns
Current:
No value
Voltage:
No value
Step Size:
No value microns
Scan Size Width:
No value microns
Sample Tilt:
No value degress
Vertical Direction:
No value
Acquisition Time:
No value
Working Distance:
No value mm
Files
Receive Materials from Timet (1)
Manufacturer:
Timet
Manufacturing Date:
No value
Production Method:
No value
Supplier:
No value
Small Fatigue Crack Growth (1)
Test Environment:
Air
Power Control:
No value
Max Stress:
No value MPa
Amplifiers Count:
No value
Resonating Frequency:
No value kHz
Test Temperature:
25 C
Calibration Constant:
No value
Stress Ratio:
-1
Files
Tensile Test (1)
Sample Geometry:
{ "name": "Cylindrical", "value": "cylindrical" }
Force Type:
{ "name": "Screw", "value": "screw" }
Test Rate:
10^-4/s
Gage Length:
10 mm
Control Mode:
{ "name": "Displacement", "value": "displacement" }
Temperature:
25 C
Files
Ultrasonic Fatigue Lifetime (1)
Calibration Constant:
No value
Max Stress:
No value MPa
Test Temperature:
25 C
Power Control:
No value
Stress Ratio:
-1
Test Environment:
Air
Amplifiers Count:
No value
Resonating Frequency:
No value kHz
Files