Sample: Pure_d34 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67375
EBSD (1)
Scan date:
9/8/2020
Scan Width:
4000 µm
Scan Height:
1000 µm
Step size:
1.5 µm
frames per second:
94 fps
Working Distance:
20 mm
Quick grain diameter - OM:
29.7 µm
Total Grains:
21.4
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files
Gleeble (1)
Test date:
9/3/2020
Start Length:
19.96 mm
Start Width:
15 mm
Start Thickness:
9.75 mm
Final Thickness:
1.88 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files
Grain Analysis (1)
Analysis Date:
11/12/2021
Input file:
USAMP_pure_D34_scan20200908A.osc
Used in histogram:
Y
Rough starting grain size:
1.2 mm
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files
Optical Microscopy (5)
Date:
9/8/2020
Objective Mag:
5
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
10
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files
Texture (1)
Basal PF Max:
12 MRD
Measurements
Alloy:
Unalloyed Mg
Total grains:
5239
Mean diameter:
23.3 µm
Median diameter:
16.9 µm
Max diameter:
319.3 µm
Files