Sample: Pure_d34RX Ungroup Processes
EBSD (1)
- Scan date:
- 9/9/2020
- Scan Width:
- 4000 µm
- Scan Height:
- 1000 µm
- Step size:
- 1.5 µm
- frames per second:
- 94 fps
- Working Distance:
- 18 mm
- Quick grain diameter - OM:
- 13.7 µm
- Total Grains:
- 86.9
- Sample orientation vertical direction:
- RD
- Voltage:
- 30 kV
- Beam Intensity or current:
- 20
Measurements
- Alloy:
- Unalloyed Mg
Files
Gleeble (1)
- Test date:
- 9/3/2020
- Start Length:
- 19.96 mm
- Start Width:
- 15 mm
- Start Thickness:
- 9.75 mm
- Final Thickness:
- 1.88 mm
- Deformations:
- 10
- Program Strain Type:
- TRUE
- Pre-deformation Soak Temp:
- 350 ºC
- Rate to Temp:
- 5 ºC/s
- Pre-deformation Soak Time:
- 600 s
- Initial Strain Rate:
- 0.5 /s
- Strain Per pass:
- 0.2
- Stage One - Temp during Deformations:
- 350 ºC
- Stage One - interpass anneal Temp:
- 350 ºC
- Stage One - interpass anneal Time:
- 600 s
- Stage Two - Number of passes:
- 0
- Quench Duration:
- 30 s
Measurements
- Alloy:
- Unalloyed Mg
Files
Heat Treatment (1)
- Furnace:
- Thermolyne
- Temperature:
- 350 ºC
- Time:
- 30 minutes
- Quench:
- Water
Measurements
- Alloy:
- Unalloyed Mg
Optical Microscopy (5)
- Date:
- 9/8/2020
- Objective Mag:
- 100
- Objective Mag:
- 50
- Objective Mag:
- 20
- Objective Mag:
- 10
- Objective Mag:
- 5
Measurements
- Alloy:
- Unalloyed Mg
Files
Receive Samples (1)
- Receipt Date:
- 11/2/2018
- Source:
- University of Florida
Measurements
- Alloy:
- Unalloyed Mg
Files
Texture (1)
- Basal PF Max:
- 14 MRD
Measurements
- Alloy:
- Unalloyed Mg