Sample: ZX00_d31 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67377
EBSD (6)
Scan date:
6/24/2020
Scan date:
7/29/2020
Scan Width:
800 µm
Scan Width:
500 µm
Scan Width:
100 µm
Scan Width:
2000 µm
Scan Height:
800 µm
Scan Height:
100 µm
Scan Height:
500 µm
Scan Height:
1000 µm
Step size:
3 µm
Step size:
1.2 µm
Step size:
0.7 µm
Step size:
1 µm
Working Distance:
20 mm
frames per second:
42 fps
Quick grain diameter - OM:
7.4 µm
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
11.1 µm
Quick grain diameter - OM:
3.6 µm
Quick grain diameter - OM:
20.9 µm
Total Grains:
18.7
Voltage:
30 kV
Total Grains:
31.67
Total Grains:
35.97
Total Grains:
28.22
Beam Intensity or current:
20
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
X0
Total grains:
272
Total grains:
1739
Composition Ca content:
0.1 wt%
Mean diameter:
29.8 µm
Mean diameter:
26.9 µm
Median diameter:
10.8 µm
Median diameter:
22.4 µm
Max diameter:
229 µm
Max diameter:
297 µm
Files
Gleeble (1)
Test date:
6/19/2020
Final Thickness:
1.75 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
X0
Total grains:
1739
Total grains:
272
Composition Ca content:
0.1 wt%
Mean diameter:
26.9 µm
Mean diameter:
29.8 µm
Median diameter:
22.4 µm
Median diameter:
10.8 µm
Max diameter:
229 µm
Max diameter:
297 µm
Files
Grain Analysis (2)
Analysis Date:
11/12/2021
Input file:
USAMP_ZX00_D31_scan20200729A.osc
Input file:
USAMP_ZX00_D31_scan20200624G.osc
Used in histogram:
N
Used in histogram:
Y
Rough starting grain size:
1.9 mm
Measurements
Alloy:
X0
Total grains:
272
Total grains:
1739
Composition Ca content:
0.1 wt%
Mean diameter:
29.8 µm
Mean diameter:
26.9 µm
Median diameter:
22.4 µm
Median diameter:
10.8 µm
Max diameter:
297 µm
Max diameter:
229 µm
Files
Optical Microscopy (3)
Date:
6/30/2020
Objective Mag:
100
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
X0
Total grains:
272
Total grains:
1739
Composition Ca content:
0.1 wt%
Mean diameter:
26.9 µm
Mean diameter:
29.8 µm
Median diameter:
10.8 µm
Median diameter:
22.4 µm
Max diameter:
229 µm
Max diameter:
297 µm
Files
Receive Samples (1)
Where:
Qianying
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
X0
Total grains:
1739
Total grains:
272
Composition Ca content:
0.1 wt%
Mean diameter:
26.9 µm
Mean diameter:
29.8 µm
Median diameter:
10.8 µm
Median diameter:
22.4 µm
Max diameter:
229 µm
Max diameter:
297 µm
Files
Texture (1)
Basal PF Max:
14 MRD
Measurements
Alloy:
X0
Total grains:
272
Total grains:
1739
Composition Ca content:
0.1 wt%
Mean diameter:
29.8 µm
Mean diameter:
26.9 µm
Median diameter:
22.4 µm
Median diameter:
10.8 µm
Max diameter:
297 µm
Max diameter:
229 µm
Files