Sample: ZX00_d31RX Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67378
EBSD (4)
Scan date:
6/26/2020
Scan date:
9/11/2020
Scan Width:
800 µm
Scan Width:
2000 µm
Scan Height:
800 µm
Scan Height:
1000 µm
Step size:
1.2 µm
Step size:
3 µm
frames per second:
53 fps
frames per second:
94 fps
Working Distance:
20 mm
Quick grain diameter - OM:
46.6 µm
Quick grain diameter - OM:
52 µm
Quick grain diameter - OM:
73 µm
Quick grain diameter - OM:
78.8 µm
Total Grains:
51.8
Total Grains:
54.2
Total Grains:
74.7
Total Grains:
68
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test date:
6/19/2020
Final Thickness:
1.75 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Files
Heat Treatment (1)
Date:
6/22/2020
Furnace:
Thermolyne
Temperature:
350 ºC
Time:
30 minutes
Quench:
Water
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Optical Microscopy (2)
Date:
6/30/2020
Objective Mag:
100
Objective Mag:
10
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Files
Texture (1)
Basal PF Max:
13 MRD
Measurements
Alloy:
X0
Composition Ca content:
0.1 wt%
Files