Sample: ZX01_d33 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67379
EBSD (4)
Scan date:
9/9/2020
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Height:
1000 µm
Scan Height:
800 µm
Step size:
1.2 µm
Step size:
3 µm
frames per second:
94 fps
Working Distance:
19 mm
Quick grain diameter - OM:
11.4 µm
Quick grain diameter - OM:
15.4 µm
Quick grain diameter - OM:
9.8 µm
Total Grains:
70
Total Grains:
112.7
Total Grains:
79.2
Total Grains:
71.6
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
X1
Total grains:
72
Total grains:
200
Composition Ca content:
0.3 wt%
Mean diameter:
90.4 µm
Mean diameter:
81.3 µm
Median diameter:
58.4 µm
Median diameter:
68.3 µm
Max diameter:
346 µm
Max diameter:
310.5 µm
Files
Gleeble (1)
Test date:
8/31/2020
Start Length:
20.12 mm
Start Width:
15.29 mm
Start Thickness:
10.01 mm
Final Thickness:
1.7 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
X1
Total grains:
200
Total grains:
72
Composition Ca content:
0.3 wt%
Mean diameter:
81.3 µm
Mean diameter:
90.4 µm
Median diameter:
68.3 µm
Median diameter:
58.4 µm
Max diameter:
346 µm
Max diameter:
310.5 µm
Files
Grain Analysis (2)
Analysis Date:
11/12/2021
Input file:
USAMP_ZX01_D33_scan20200909A.osc
Input file:
USAMP_ZX01_D33_scan20200909B.osc
Used in histogram:
N
Used in histogram:
Y
Rough starting grain size:
1.6 mm
Measurements
Alloy:
X1
Total grains:
72
Total grains:
200
Composition Ca content:
0.3 wt%
Mean diameter:
90.4 µm
Mean diameter:
81.3 µm
Median diameter:
68.3 µm
Median diameter:
58.4 µm
Max diameter:
310.5 µm
Max diameter:
346 µm
Files
Optical Microscopy (9)
Date:
9/10/2020
Date:
9/2/2020
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
X1
Total grains:
72
Total grains:
200
Composition Ca content:
0.3 wt%
Mean diameter:
81.3 µm
Mean diameter:
90.4 µm
Median diameter:
58.4 µm
Median diameter:
68.3 µm
Max diameter:
346 µm
Max diameter:
310.5 µm
Files
Receive Samples (1)
Receipt Date:
8/31/2020
Source:
University of Florida
Measurements
Alloy:
X1
Total grains:
200
Total grains:
72
Composition Ca content:
0.3 wt%
Mean diameter:
81.3 µm
Mean diameter:
90.4 µm
Median diameter:
58.4 µm
Median diameter:
68.3 µm
Max diameter:
346 µm
Max diameter:
310.5 µm
Files
Texture (1)
Basal PF Max:
14 MRD
Measurements
Alloy:
X1
Total grains:
72
Total grains:
200
Composition Ca content:
0.3 wt%
Mean diameter:
90.4 µm
Mean diameter:
81.3 µm
Median diameter:
68.3 µm
Median diameter:
58.4 µm
Max diameter:
310.5 µm
Max diameter:
346 µm