Sample: ZX01_d33RX Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67380
EBSD (4)
Scan date:
9/4/2020
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Height:
800 µm
Scan Height:
1000 µm
Step size:
3 µm
Step size:
1.2 µm
frames per second:
94 fps
Working Distance:
20 mm
Quick grain diameter - OM:
68.6 µm
Quick grain diameter - OM:
35.7 µm
Quick grain diameter - OM:
55.8 µm
Quick grain diameter - OM:
54.6 µm
Total Grains:
66.2
Total Grains:
99.5
Total Grains:
81.6
Total Grains:
85.8
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Files
Gleeble (1)
Test date:
8/31/2020
Start Length:
20.12 mm
Start Width:
15.29 mm
Start Thickness:
10.01 mm
Final Thickness:
1.7 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Files
Heat Treatment (1)
Date:
9/1/2020
Furnace:
Thermolyne
Temperature:
350 ºC
Time:
30 minutes
Quench:
Water
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Optical Microscopy (8)
Date:
9/10/2020
Date:
9/2/2020
Objective Mag:
10
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
5
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Files
Receive Samples (1)
Receipt Date:
8/31/2020
Source:
University of Florida
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Files
Texture (1)
Basal PF Max:
13 MRD
Measurements
Alloy:
X1
Composition Ca content:
0.3 wt%
Files