Sample: ZX21_d30 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67382
EBSD (6)
Scan date:
7/21/2020
Scan Width:
200 µm
Scan Width:
800 µm
Scan Width:
2000 µm
Scan Height:
200 µm
Scan Height:
800 µm
Scan Height:
1000 µm
Step size:
1.2 µm
Step size:
0.5 µm
Step size:
3 µm
frames per second:
111 fps
frames per second:
86 fps
Working Distance:
21 mm
Quick grain diameter - OM:
30.7 µm
Quick grain diameter - OM:
44.8 µm
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
0.07 µm
Quick grain diameter - OM:
46.4 µm
Quick grain diameter - OM:
43.3 µm
Total Grains:
30.88
Voltage:
30 kV
Sample orientation vertical direction:
RD
Total Grains:
25.2
Total Grains:
31.08
Total Grains:
31.5
Voltage:
30 kV
Sample orientation vertical direction:
RD
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Beam Intensity or current:
20
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files
Gleeble (1)
Test date:
6/15/2020
Start Length:
20.1 mm
Start Width:
15.25 mm
Start Thickness:
9.87 mm
Final Thickness:
1.74 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files
Grain Analysis (1)
Analysis Date:
11/12/2021
Input file:
USAMP_ZX21_D30_scan20200721B.osc
Used in histogram:
Y
Rough starting grain size:
1.1 mm
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files
Optical Microscopy (4)
Date:
6/16/2020
Date:
7/15/2020
Date:
6/30/2020
Objective Mag:
100
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files
Texture (1)
Basal PF Max:
3.3 MRD
Measurements
Alloy:
ZX21
Total grains:
882
Composition Zn content:
1.9 wt%
Mean diameter:
25.8 µm
Composition Ca content:
0.3 wt%
Median diameter:
23 µm
Max diameter:
88.5 µm
Files