Sample: ZX21_d30RX Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67383
EBSD (5)
Scan date:
6/24/2020
Scan date:
6/17/2020
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Height:
1000 µm
Scan Height:
800 µm
Step size:
3 µm
Step size:
0.8 µm
Step size:
1.2 µm
frames per second:
23 fps
frames per second:
38 fps
frames per second:
73 fps
Quick grain diameter - OM:
90.3 µm
Quick grain diameter - OM:
91.5 µm
Quick grain diameter - OM:
91 µm
Quick grain diameter - OM:
91.3 µm
Working Distance:
22 mm
Total Grains:
12.7
Total Grains:
18.6
Quick grain diameter - OM:
95.1 µm
Total Grains:
18.9
Total Grains:
18
Sample orientation vertical direction:
RD
Total Grains:
11.7
Voltage:
30 kV
Sample orientation vertical direction:
RD
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Files
Gleeble (1)
Test date:
6/15/2020
Start Length:
20.1 mm
Start Width:
15.25 mm
Start Thickness:
9.87 mm
Final Thickness:
1.74 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Files
Heat Treatment (1)
Date:
6/15/2020
Furnace:
Thermolyne
Temperature:
350 ºC
Time:
30 minutes
Quench:
Water
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Optical Microscopy (5)
Date:
6/16/2020
Date:
6/30/2020
Objective Mag:
5
Objective Mag:
10
Objective Mag:
50
Objective Mag:
100
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Files
Texture (1)
Basal PF Max:
3.8 MRD
Measurements
Alloy:
ZX23
Composition Zn content:
1.9 wt%
Composition Ca content:
0.3 wt%
Files