Sample: ZX30_d21 Ungroup Processes
Last Updated: 1 month ago Owner: Tracy Berman ID: 67384
EBSD (10)
Settings
Scan date:
7/4/2023
Scan date:
7/2/2023
Scan date:
12/21/2020
Scan date:
10/9/2020
Scan date:
9/21/2020
Scan date:
1/3/2020
Scan date:
1/2/2020
Scan Width:
100 µm
Scan Width:
200 µm
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Width:
300 µm
Scan Height:
100 µm
Scan Height:
200 µm
Scan Height:
300 µm
Scan Height:
800 µm
Step size:
1 µm
Step size:
3 µm
Step size:
1.2 µm
Step size:
1.5 µm
Step size:
0.2 µm
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
0.1 µm
frames per second:
30 fps
frames per second:
50 fps
frames per second:
47 fps
frames per second:
23 fps
frames per second:
24 fps
frames per second:
25 fps
Quick grain diameter - OM:
0.4 µm
Quick grain diameter - OM:
0.2 µm
Total Grains:
27.7
Working Distance:
18 mm
Sample orientation vertical direction:
RD
Voltage:
30 kV
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
5.7 µm
Beam Intensity or current:
20
Total Grains:
24.5
Total Grains:
26.2
Voltage:
30 kV
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Total Grains:
5.54
Voltage:
30 kV
Beam Intensity or current:
20
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
Gleeble (1)
Settings
Test date:
11/25/2019
Start Length:
20.17 mm
Start Width:
15.19 mm
Start Thickness:
9.82 mm
Final Thickness:
1.7 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
Grain Analysis (1)
Settings
Analysis Date:
11/12/2021
Input file:
USAMP_ZX30D21_scan20200102A.osc
Used in histogram:
Y
Rough starting grain size:
1.1 mm
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
Optical Microscopy (10)
Settings
Date:
12/17/2020
Date:
7/10/2020
Objective Mag:
100
Objective Mag:
50
Objective Mag:
10
Objective Mag:
20
Objective Mag:
5
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
Receive Samples (1)
Settings
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
SEM (7)
Settings
Date:
9/18/2020
Mode:
BSE
Voltage:
20 kV
View Field:
100 µm
View Field:
50 µm
View Field:
20 µm
Sample orientation - vertical direction:
RD
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files
Texture (1)
Settings
Basal PF Max:
4.6 MRD
Measurements
Alloy:
ZX30
Total grains:
1181
Composition Zn content:
3.2 wt%
Mean diameter:
22.5 µm
Composition Ca content:
0.1 wt%
Median diameter:
19 µm
Max diameter:
87.9 µm
Files