Sample: ZX30_d21RX Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67385
EBSD (4)
Scan date:
2/8/2020
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Height:
1000 µm
Scan Height:
800 µm
Step size:
3 µm
Step size:
1.2 µm
frames per second:
50 fps
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test date:
11/25/2019
Start Length:
20.17 mm
Start Width:
15.19 mm
Start Thickness:
9.82 mm
Final Thickness:
1.7 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Heat Treatment (1)
Furnace:
Thermolyne
Temperature:
350 ºC
Time:
10 minutes
Quench:
Water
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Optical Microscopy (5)
Date:
7/10/2020
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Texture (1)
Basal PF Max:
2.8 MRD
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files