Sample: ZX30_d29_350C_30min Ungroup Processes
EBSD (5)
- Scan date:
- 6/11/2020
- Scan date:
- 7/15/2020
- Scan Width:
- 800 µm
- Scan Width:
- 2000 µm
- Scan Height:
- 800 µm
- Scan Height:
- 1000 µm
- Step size:
- 1.2 µm
- Step size:
- 3 µm
- frames per second:
- 73 fps
- Working Distance:
- 22 mm
- Working Distance:
- 20 mm
- Quick grain diameter - OM:
- 96.8 µm
- Quick grain diameter - OM:
- 92.6 µm
- Quick grain diameter - OM:
- 98.2 µm
- Quick grain diameter - OM:
- 98.4 µm
- Quick grain diameter - OM:
- 98.1 µm
- Total Grains:
- 32.2
- Total Grains:
- 32.01
- Total Grains:
- 30.22
- Sample orientation vertical direction:
- RD
- Sample orientation vertical direction:
- RD
- Voltage:
- 30 kV
- Voltage:
- 30 kV
- Beam Intensity or current:
- 20
- Beam Intensity or current:
- 20
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%
Files
- USAMP_ZX30D29_350C_30min_scan20200611A_GF1.txt
- USAMP_ZX30D29_350C_30min_scan20200611A_GF2.txt
-
USAMP_ZX30D29_350C_30min_scan20200611A_GOS_Legend.jpg
-
USAMP_ZX30D29_350C_30min_scan20200611A_GOS.jpg
-
USAMP_ZX30D29_350C_30min_scan20200611A_IPFmap.jpg
- USAMP_ZX30D29_350C_30min_scan20200611A.osc
- USAMP_ZX30D29_350C_30min_scan20200611B_GF1.txt
- USAMP_ZX30D29_350C_30min_scan20200611B_GF2.txt
-
USAMP_ZX30D29_350C_30min_scan20200611B_GOS_Legend.jpg
-
USAMP_ZX30D29_350C_30min_scan20200611B_GOS.jpg
-
USAMP_ZX30D29_350C_30min_scan20200611B_IPFmap.jpg
- USAMP_ZX30D29_350C_30min_scan20200611B.osc
- USAMP_ZX30D29_350C_30min_scan20200715A.osc
- USAMP_ZX30D29_350C_30min_scan20200715B.osc
- USAMP_ZX30D29_350C_30min_scan20200715C.osc See 4 more files......
Gleeble (1)
- Test date:
- 3/16/2020
- Start Length:
- 20.05 mm
- Start Width:
- 15.17 mm
- Start Thickness:
- 9.85 mm
- Final Thickness:
- 1.9 mm
- Deformations:
- 10
- Program Strain Type:
- TRUE
- Pre-deformation Soak Temp:
- 350 ºC
- Rate to Temp:
- 5 ºC/s
- Pre-deformation Soak Time:
- 600 s
- Initial Strain Rate:
- 0.5 /s
- Strain Per pass:
- 0.2
- Stage One - Temp during Deformations:
- 350 ºC
- Stage One - interpass anneal Temp:
- 350 ºC
- Stage One - interpass anneal Time:
- 600 s
- Stage Two - Number of passes:
- 0
- Quench Duration:
- 30 s
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%
Files
Heat Treatment (1)
- Date:
- 6/9/2020
- Furnace:
- Thermolyne
- Temperature:
- 350 ºC
- Time:
- 30 minutes
- Quench:
- Water
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%
Optical Microscopy (3)
- Date:
- 7/10/2020
- Objective Mag:
- 100
- Objective Mag:
- 10
- Objective Mag:
- 5
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%
Files
Receive Samples (1)
- Receipt Date:
- 11/2/2018
- Source:
- University of Florida
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%
Files
Texture (1)
- Basal PF Max:
- 1.9 MRD
Measurements
- Alloy:
- ZX30
- Composition Zn content:
- 3.2 wt%
- Composition Ca content:
- 0.1 wt%