Sample: ZX31_d32 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67387
EBSD (6)
Scan date:
7/28/2020
Scan date:
7/1/2020
Scan Width:
800 µm
Scan Width:
200 µm
Scan Width:
150 µm
Scan Width:
2000 µm
Scan Height:
150 µm
Scan Height:
800 µm
Scan Height:
200 µm
Scan Height:
1000 µm
Step size:
0.5 µm
Step size:
0.2 µm
Step size:
1.2 µm
Step size:
3 µm
frames per second:
73 fps
frames per second:
23 fps
Working Distance:
22 mm
Sample orientation vertical direction:
RD
Working Distance:
20 mm
Quick grain diameter - OM:
2.5 µm
Voltage:
30 kV
Quick grain diameter - OM:
28.7 µm
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
45.4 µm
Total Grains:
38.71
Quick grain diameter - OM:
0.007 µm
Beam Intensity or current:
20
Voltage:
30 kV
Total Grains:
36.23
Total Grains:
6.3
Total Grains:
17.2
Beam Intensity or current:
20
Sample orientation vertical direction:
RD
Voltage:
30 kV
Sample orientation vertical direction:
RD
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
Gleeble (1)
Test date:
6/26/2020
Start Length:
20.11 mm
Start Width:
15.24 mm
Start Thickness:
9.85 mm
Final Thickness:
1.77 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
Grain Analysis (1)
Analysis Date:
11/12/2021
Input file:
USAMP_ZX31_D32_scan2020701A.osc
Used in histogram:
Y
Rough starting grain size:
1.2 mm
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
Optical Microscopy (2)
Date:
6/30/2020
Objective Mag:
100
Objective Mag:
10
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
SEM (4)
Date:
2/12/2021
Mode:
BSE
Voltage:
20 kV
View Field:
1000 µm
View Field:
100 µm
Sample orientation - vertical direction:
RD
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files
Texture (1)
Basal PF Max:
3.4 MRD
Measurements
Alloy:
ZX31
Total grains:
1436
Composition Zn content:
3.2 wt%
Mean diameter:
20.7 µm
Composition Ca content:
0.3 wt%
Median diameter:
17.9 µm
Max diameter:
71.8 µm
Files