Sample: ZX31_d32RX Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67388
EBSD (4)
Scan date:
7/1/2020
Scan date:
7/15/2020
Scan Width:
800 µm
Scan Width:
2000 µm
Scan Height:
800 µm
Scan Height:
1000 µm
Step size:
1.2 µm
Step size:
3 µm
Quick grain diameter - OM:
92.3 µm
frames per second:
73 fps
Working Distance:
22 mm
Total Grains:
19.5
Sample orientation vertical direction:
RD
Quick grain diameter - OM:
92.4 µm
Quick grain diameter - OM:
92.6 µm
Quick grain diameter - OM:
94.6 µm
Total Grains:
24.1
Voltage:
30 kV
Total Grains:
24.85
Total Grains:
24.4
Sample orientation vertical direction:
RD
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Files
Gleeble (1)
Test date:
6/26/2020
Start Length:
20.11 mm
Start Width:
15.24 mm
Start Thickness:
9.85 mm
Final Thickness:
1.77 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Files
Heat Treatment (1)
Date:
6/29/2020
Furnace:
Thermolyne
Temperature:
350 ºC
Time:
30 minutes
Quench:
Water
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Optical Microscopy (2)
Date:
6/30/2020
Objective Mag:
100
Objective Mag:
10
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Files
Texture (1)
Basal PF Max:
2.1 MRD
Measurements
Alloy:
ZX31
Composition Zn content:
3.2 wt%
Composition Ca content:
0.3 wt%
Files