Sample: ZX30_8v4D04 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67390
EBSD (9)
Scan date:
1/31/24
Scan date:
10/4/21
Scan date:
10/01/21
Scan date:
6/4/21
SEM View Field:
1120 µm
Scan Width:
800 µm
Scan Width:
400 µm
Scan Width:
2000 µm
Scan Height:
1000 µm
Scan Width:
800 µm
Scan Height:
400 µm
Scan Height:
800 µm
Step size:
5 µm
Step size:
3 µm
Step size:
1.5 µm
Scan Height:
800 µm
frames per second:
134 fps
frames per second:
86 fps
Step size:
1 µm
frames per second:
105 fps
frames per second:
19 fps
Total Fraction Less than 1º:
95.2 %
Total Fraction Less than 1º:
64 %
Total Fraction Less than 1º:
81.1 %
Sample orientation vertical direction:
RD/ED
Total Fraction Less than 1º:
98.4 %
Total Fraction Less than 1º:
29.8 %
frames per second:
150 fps
Number of grains:
1136
Number of grains:
1118
Number of grains:
547
collection time:
1.5
Voltage:
30 kV
Number of grains:
408
Number of grains:
939
Total Fraction Less than 1º:
81.4 %
Beam Intensity or current:
20
Average Diameter:
55.5 µm
Average Diameter:
21 µm
Average Diameter:
41.5 µm
Average Diameter:
40.4 µm
Average Diameter:
28 µm
Number of grains:
787
Sample orientation vertical direction:
RD/ED
Average Diameter:
28 µm
Voltage:
30 kV
Sample orientation vertical direction:
RD/ED
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Basal PF Max:
2.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test Date:
6/1/21
Final thickness:
2.67 mm
Pre-deformation soak Temp:
350
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Number of passes:
4
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
4
Stage Two - Temp during Deformations:
325 ºC
Stage Two - interpass anneal Temp:
325 ºC
Stage Two - interpass anneal Time:
300 s
Post-deformation Soak Temp:
325 ºC
Post-deformation Soak Time:
1800 s
Deformations:
8
Quench Duration:
30 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Measurements
Alloy:
ZX30
Basal PF Max:
2.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Optical Microscopy (5)
Date:
6/2/2021
Objective Mag:
5
Objective Mag:
10
Objective Mag:
20
Objective Mag:
50
Objective Mag:
100
Measurements
Alloy:
ZX30
Basal PF Max:
2.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/18
Source:
University of Florida
Solution treatment time:
24 hr
Solution treatment Temp:
350 ºC
Measurements
Alloy:
ZX30
Basal PF Max:
2.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Texture (1)
Measurements
Alloy:
ZX30
Basal PF Max:
2.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files