Sample: ZX31_8v2D01_325C_30min Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67391
EBSD (5)
Scan date:
5/18/21
Scan date:
2/2/24
Scan date:
10/1/21
Scan Width:
2000 µm
Scan Width:
800 µm
SEM View Field:
1120 µm
Scan Height:
1000 µm
Scan Height:
800 µm
Scan Width:
800 µm
Total Fraction Less than 1º:
96.6 %
Step size:
3 µm
Scan Height:
800 µm
frames per second:
105 fps
Step size:
1 µm
Sample orientation vertical direction:
RD/ED
Total Fraction Less than 1º:
82.1 %
Total Fraction Less than 1º:
79.9 %
frames per second:
135 fps
Voltage:
30 kV
Total Fraction Less than 1º:
61 %
Number of grains:
3384
Number of grains:
3339
Beam Intensity or current:
20
Number of grains:
2789
collection time:
1.5
Average Diameter:
24.6 µm
Average Diameter:
24.03 µm
Average Diameter:
24.7 µm
Total Fraction Less than 1º:
80.4 %
Sample orientation vertical direction:
RD/ED
Number of grains:
1728
Voltage:
30 kV
Average Diameter:
19 µm
Beam Intensity or current:
20
Sample orientation vertical direction:
RD/ED
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test Date:
5/10/21
Initial length:
19.95 mm
Initial width:
15.3 mm
Initial thickness:
9.87 mm
Final thickness:
2.56 mm
Pre-deformation soak Temp:
350
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Number of passes:
4
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
4
Stage Two - Temp during Deformations:
325 ºC
Stage Two - interpass anneal Temp:
325 ºC
Stage Two - interpass anneal Time:
300 s
Deformations:
8
Quench Duration:
30 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Heat Treatment (1)
Date:
5/12/21
Who did the treatment:
Tracy
Furnace:
Thermolyne
Temperature:
325 ºC
Time:
30 minutes
Quench:
Water
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Optical Microscopy (1)
Date:
5/14/2021
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/18
Source:
University of Florida
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Texture (1)
Measurements
Alloy:
ZX31
Basal PF Max:
3.3 MRD
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files