Sample: ZX0p50_8pass_d02 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67393
EBSD (5)
Scan date:
11/4/22
Scan date:
1/31/24
SEM View Field:
1120 µm
Scan Width:
2000 µm
Scan Width:
800 µm
Scan Width:
800 µm
Scan Height:
800 µm
Scan Height:
1000 µm
Scan Height:
800 µm
Step size:
3 µm
Step size:
5 µm
Step size:
1 µm
frames per second:
110 fps
frames per second:
150 fps
collection time:
0.5
Total Fraction Less than 1º:
27.7 %
Total Fraction Less than 1º:
38.1 %
Total Fraction Less than 1º:
35.6 %
collection time:
1.5
Total Fraction Less than 1º:
35 %
Total Fraction Less than 1º:
56.3 %
Number of grains:
987
Number of grains:
1380
Number of grains:
1363
Number of grains:
605
Number of grains:
155
Average Diameter:
32 µm
Average Diameter:
44 µm
Average Diameter:
39 µm
Sample orientation vertical direction:
RD/ED
Average Diameter:
60 µm
Voltage:
30 kV
Sample orientation vertical direction:
RD/ED
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX0p50
Basal PF Max:
12 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test Date:
11/2/2022
Initial length:
20.24 mm
Initial width:
15.2 mm
Initial thickness:
10.01 mm
Final thickness:
2.51 mm
Pre-deformation soak Temp:
350
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Number of passes:
4
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
4
Stage Two - Temp during Deformations:
325 ºC
Stage Two - interpass anneal Temp:
325 ºC
Stage Two - interpass anneal Time:
300 s
Post-deformation Soak Temp:
325 ºC
Post-deformation Soak Time:
1800 s
Deformations:
8
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Measurements
Alloy:
ZX0p50
Basal PF Max:
12 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/18
Source:
University of Florida
Measurements
Alloy:
ZX0p50
Basal PF Max:
12 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Texture (1)
Measurements
Alloy:
ZX0p50
Basal PF Max:
12 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files