Sample: unalloyed_8v4_d08 Ungroup Processes
EBSD (3)
- Scan date:
- 1/20/24
- Scan date:
- 1/31/24
- Scan Width:
- 800 µm
- SEM View Field:
- 2050 µm
- Scan Width:
- 1971 µm
- Scan Height:
- 800 µm
- Scan Height:
- 1000 µm
- Step size:
- 1 µm
- Step size:
- 5 µm
- Total Fraction Less than 1º:
- 34.5 %
- frames per second:
- 150 fps
- Number of grains:
- 234
- Average Diameter:
- 48 µm
- collection time:
- 0.25
- Sample orientation vertical direction:
- RD/ED
- Voltage:
- 30 kV
- Beam Intensity or current:
- 20
Measurements
- Alloy:
- Unalloyed Mg
- Composition Zn content:
- 0 wt%
- Composition Ca content:
- 0 wt%
Files
Gleeble (1)
- Test Date:
- 12/20/2023
- Initial length:
- 19.97 mm
- Initial width:
- 15.27 mm
- Initial thickness:
- 9.8 mm
- Final thickness:
- 2.36 mm
- Final length:
- 23.35 mm
- Pre-deformation soak Temp:
- 350
- Initial Strain Rate:
- 0.5 /s
- Strain Per pass:
- 0.2
- Stage One - Number of passes:
- 4
- Stage One - Temp during Deformations:
- 350 ºC
- Stage One - interpass anneal Temp:
- 350 ºC
- Stage One - interpass anneal Time:
- 600 s
- Stage Two - Number of passes:
- 4
- Stage Two - Temp during Deformations:
- 325 ºC
- Stage Two - interpass anneal Temp:
- 325 ºC
- Stage Two - interpass anneal Time:
- 300 s
- Post-deformation Soak Temp:
- 325 ºC
- Post-deformation Soak Time:
- 1800 s
- Deformations:
- 8
- Quench Duration:
- 45 s
- Rate to Temp:
- 5 ºC/s
- Program Strain Type:
- TRUE
- Pre-deformation Soak Time:
- 600 s
Measurements
- Alloy:
- Unalloyed Mg
- Composition Zn content:
- 0 wt%
- Composition Ca content:
- 0 wt%
Files
Receive Samples (1)
- Receipt Date:
- 11/2/18
- Source:
- University of Florida
Measurements
- Alloy:
- Unalloyed Mg
- Composition Zn content:
- 0 wt%
- Composition Ca content:
- 0 wt%
Files
Texture (1)
Measurements
- Alloy:
- Unalloyed Mg
- Composition Zn content:
- 0 wt%
- Composition Ca content:
- 0 wt%