Sample: ZX0p50_PSC5_d10 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67395
EBSD (7)
Scan date:
4/1/24
Scan date:
1/29/24
SEM View Field:
1120 µm
SEM View Field:
2200 µm
SEM View Field:
2000 µm
Scan Width:
800 µm
Scan Width:
1971 µm
Scan Width:
2180 µm
Scan Height:
1490 µm
Scan Height:
800 µm
Scan Height:
1650 µm
Step size:
5 µm
Step size:
1 µm
Step size:
6 µm
frames per second:
80 fps
frames per second:
110 fps
frames per second:
135 fps
collection time:
0.75
collection time:
1.75
collection time:
0.33
Total Fraction Less than 1º:
42.7 %
Sample orientation vertical direction:
RD/ED
Voltage:
30 kV
Number of grains:
750
Beam Intensity or current:
20
Average Diameter:
26.4 µm
Sample orientation vertical direction:
RD/ED
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX0p50
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test Date:
12/20/2023
Initial length:
19.96 mm
Initial width:
15.19 mm
Initial thickness:
10.01 mm
Final thickness:
4.15 mm
Final length:
22.78 mm
Pre-deformation soak Temp:
350
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Number of passes:
5
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Deformations:
5
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Measurements
Alloy:
ZX0p50
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/18
Source:
University of Florida
Measurements
Alloy:
ZX0p50
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Texture (2)
Measurements
Alloy:
ZX0p50
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files