Sample: ZX0p50_PSC1_d04 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67396
EBSD (8)
Scan date:
4/1/24
Scan date:
3/30/24
Scan date:
2/25/24
Scan date:
1/16/24
SEM View Field:
2200 µm
Scan Width:
1184 µm
Scan Width:
1971 µm
Scan Height:
895 µm
Scan Width:
2180 µm
Scan Width:
2000 µm
Scan Height:
1489 µm
Scan Height:
1650 µm
Step size:
1 µm
Scan Height:
1000 µm
Sample orientation vertical direction:
RD/ED
Step size:
5 µm
frames per second:
135 fps
Step size:
6 µm
Voltage:
30 kV
Total Fraction Less than 1º:
13 %
frames per second:
80 fps
frames per second:
50 fps
Beam Intensity or current:
20
collection time:
0.5
collection time:
0.75
Number of grains:
585
Average Diameter:
24 µm
Sample orientation vertical direction:
RD/ED
Sample orientation vertical direction:
RD/ED
Voltage:
30 kV
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX0p50
Basal PF Max:
13 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test Date:
12/20/2023
Initial length:
20.15 mm
Initial width:
15.02 mm
Initial thickness:
9.99 mm
Final thickness:
8.3 mm
Final length:
21.16 mm
Pre-deformation soak Temp:
350
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Number of passes:
1
Stage One - Temp during Deformations:
350 ºC
Deformations:
1
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Measurements
Alloy:
ZX0p50
Basal PF Max:
13 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/18
Source:
University of Florida
Measurements
Alloy:
ZX0p50
Basal PF Max:
13 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files
Texture (2)
Measurements
Alloy:
ZX0p50
Basal PF Max:
13 MRD
Composition Zn content:
0.5 wt%
Composition Ca content:
0.1 wt%
Files