EBSD (6)

Scan date:

2/26/24

Scan date:

3/29/24

SEM View Field:

2200 µm

SEM View Field:

550 µm

SEM View Field:

1150 µm

Scan Width:

400 µm

Scan Width:

800 µm

Scan Width:

2000 µm

Scan Height:

400 µm

Scan Height:

800 µm

Scan Height:

500 µm

Step size:

1 µm

Step size:

5 µm

frames per second:

50 fps

collection time:

4

collection time:

2

collection time:

0.25

Total Fraction Less than 1º:

0.502 %

Sample orientation vertical direction:

RD/ED

CI>0.1 after rescan:

0.712

Voltage:

30 kV

Total Fraction Less than 1º:

1.5 %

Number of grains:

3358

Sample orientation vertical direction:

RD/ED

Beam Intensity or current:

20

Average Diameter:

12 µm

Voltage:

30 kV

Sample orientation vertical direction:

RD/ED

Beam Intensity or current:

20

Voltage:

30 kV

Beam Intensity or current:

20

Measurements

Alloy:

ZX31

Basal PF Max:

4.6 MRD

Composition Zn content:

3.2 wt%

Composition Ca content:

0.1 wt%

Files

• ZX31_PSC5_d09_20240226scanC.osc
• ZX31_PSC5_d09_20240226scanD.osc
• ZX31_PSC5_d09_20240226scanE.osc
• ZX31_PSC5_d09_20240226scanF.osc
• ZX31_PSC5_d09_20240226scanG_Rescan_GOS_Legend.jpg
  
• ZX31_PSC5_d09_20240226scanG_Rescan_GOS.jpg
  
• ZX31_PSC5_d09_20240226scanG_Rescan_IPFmap.jpg
  
• ZX31_PSC5_d09_20240329scanD_Rescan_GOS_Legend.jpg
  
• ZX31_PSC5_d09_20240329scanD_Rescan_GOS.jpg
  
• ZX31_PSC5_d09_20240329scanD_Rescan_IPFmap.jpg
  
• ZX31_PSC5_d09_20240329scanD_Rescan.osc
See 1 more files......

Gleeble (2)

Test Date:

12/20/2023

Initial length:

19.96 mm

Initial length:

19.98 mm

Initial width:

14.97 mm

Initial width:

15.19 mm

Initial thickness:

10.01 mm

Initial thickness:

10 mm

Final thickness:

4.17 mm

Final thickness:

4.15 mm

Final length:

22.78 mm

Final length:

22.46 mm

Pre-deformation soak Temp:

350

Initial Strain Rate:

0.5 /s

Strain Per pass:

0.2

Stage One - Number of passes:

5

Stage One - Temp during Deformations:

350 ºC

Stage One - interpass anneal Temp:

350 ºC

Stage One - interpass anneal Time:

600 s

Deformations:

5

Quench Duration:

45 s

Rate to Temp:

5 ºC/s

Program Strain Type:

TRUE

Pre-deformation Soak Time:

600 s

Measurements

Alloy:

ZX31

Basal PF Max:

4.6 MRD

Composition Zn content:

3.2 wt%

Composition Ca content:

0.1 wt%

Files

• USAMP_PSC5_d09.csv
• USAMP_PSC5_d10.csv
• USAMP_PSC5.qhd

Receive Samples (1)

Receipt Date:

11/2/18

Source:

University of Florida

Measurements

Alloy:

ZX31

Basal PF Max:

4.6 MRD

Composition Zn content:

3.2 wt%

Composition Ca content:

0.1 wt%

Files

• USAMP Ingot Compositions.xlsx

Texture (1)

Measurements

Alloy:

ZX31

Basal PF Max:

4.6 MRD

Composition Zn content:

3.2 wt%

Composition Ca content:

0.1 wt%

Files

• Texture_ZX31_PSC5_d09_IPFmap.jpg
  
• Texture_ZX31_PSC5_d09_PFmax4p5.jpg
  
• Texture_ZX31_PSC5_d09.m