Sample: ZX0p50_d39 Ungroup Processes
EBSD (4)
- Scan date:
- 11/16/2020
- Scan Width:
- 800 µm
- Scan Width:
- 2000 µm
- Scan Height:
- 800 µm
- Scan Height:
- 1000 µm
- Step size:
- 1 µm
- Step size:
- 3 µm
- frames per second:
- 60 fps
- frames per second:
- 105 fps
- Sample orientation vertical direction:
- RD
- Quick grain diameter - OM:
- 29.8 µm
- Voltage:
- 30 kV
- Sample orientation vertical direction:
- RD
- Beam Intensity or current:
- 20
- Voltage:
- 30 kV
- Beam Intensity or current:
- 20
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm
Files
Gleeble (1)
- Test date:
- 10/30/2020
- Start Length:
- 20.25 mm
- Start Width:
- 15.01 mm
- Start Thickness:
- 9.98 mm
- Final Thickness:
- 1.88 mm
- Deformations:
- 10
- Program Strain Type:
- TRUE
- Pre-deformation Soak Temp:
- 350 ºC
- Rate to Temp:
- 5 ºC/s
- Pre-deformation Soak Time:
- 600 s
- Initial Strain Rate:
- 0.5 /s
- Strain Per pass:
- 0.2
- Stage One - Temp during Deformations:
- 350 ºC
- Stage One - interpass anneal Temp:
- 350 ºC
- Stage One - interpass anneal Time:
- 600 s
- Stage Two - Number of passes:
- 0
- Quench Duration:
- 30 s
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm
Files
Grain Analysis (1)
- Analysis Date:
- 11/12/2021
- Input file:
- USAMP_ZX0p50_D39_scan20201116D.osc
- Used in histogram:
- Y
- Rough starting grain size:
- 2.2 mm
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm
Files
Optical Microscopy (3)
- Date:
- 11/13/2020
- Objective Mag:
- 100
- Objective Mag:
- 10
- Objective Mag:
- 5
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm
Files
Receive Samples (1)
- Receipt Date:
- 11/2/2018
- Source:
- University of Florida
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm
Files
Texture (1)
- Basal PF Max:
- 13 MRD
Measurements
- Alloy:
- ZX0p50
- Total grains:
- 1533
- Composition Zn content:
- 0.5 wt%
- Mean diameter:
- 17.8 µm
- Composition Ca content:
- 0.1 wt%
- Median diameter:
- 13 µm
- Max diameter:
- 139.1 µm