Sample: ZX30_1d02 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67399
EBSD (10)
Scan date:
1/7/2021
Scan date:
1/6/2021
Scan date:
11/27/2020
Scan date:
2/25/2024
Scan Width:
400 µm
Scan Width:
2000 µm
Scan Width:
1140 µm
Scan Width:
200 µm
Scan Width:
800 µm
Scan Width:
100 µm
Scan Height:
800 µm
Scan Height:
400 µm
Scan Height:
1000 µm
Scan Height:
200 µm
Scan Height:
100 µm
Scan Height:
860 µm
Step size:
0.1 µm
Step size:
0.25 µm
Step size:
5 µm
Step size:
3 µm
Step size:
0.2 µm
Step size:
2 µm
Step size:
10 µm
Step size:
1 µm
Sample orientation vertical direction:
RD
frames per second:
50 fps
frames per second:
74 fps
frames per second:
19 fps
Voltage:
30 kV
Sample orientation vertical direction:
RD
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test date:
10/30/2020
Start Length:
20.12 mm
Start Width:
15.11 mm
Start Thickness:
9.88 mm
Final Thickness:
8.4 mm
Deformations:
1
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Optical Microscopy (3)
Date:
11/13/2020
Objective Mag:
100
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Texture (1)
Basal PF Max:
7.9 MRD
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files