Sample: ZX30_5d01 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67400
EBSD (7)
Scan date:
2/23/2024
Scan date:
9/23/2020
Scan date:
10/5/2020
Scan Width:
800 µm
Scan Width:
200 µm
Scan Width:
2000 µm
Scan Height:
1000 µm
Scan Height:
200 µm
Scan Height:
800 µm
Step size:
5 µm
Step size:
0.25 µm
Step size:
1 µm
Step size:
3 µm
Sample orientation vertical direction:
RD
frames per second:
73 fps
frames per second:
37 fps
frames per second:
52 fps
Quick grain diameter - OM:
6 µm
Working Distance:
23 mm
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Voltage:
30 kV
Sample orientation vertical direction:
RD
Total Fraction Less than 1º:
24.9 %
Beam Intensity or current:
20
Voltage:
30 kV
Quick grain diameter - OM:
649 µm
Beam Intensity or current:
20
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Gleeble (1)
Test date:
9/15/2020
Start Length:
20.18 mm
Start Width:
15.08 mm
Start Thickness:
9.82 mm
Final Thickness:
4.19 mm
Deformations:
5
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Post-deformation soak Temp:
0 ºC
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Optical Microscopy (4)
Date:
9/22/2020
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
10
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files
Texture (2)
Basal PF Max:
6.2 MRD
Basal PF Max:
4 MRD
Measurements
Alloy:
ZX30
Composition Zn content:
3.2 wt%
Composition Ca content:
0.1 wt%
Files