Sample: ZX30_TD350_AS-DEF Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67401
EBSD (10)
Scan date:
11/4/22
Scan date:
8/29/22
frames per second:
46 fps
Scan Width:
125 µm
Scan Width:
2000 µm
Scan Width:
400 µm
Scan Height:
1000 µm
EBSD Camera Binning:
1 x 1
Scan Height:
500 µm
Scan Height:
400 µm
Scan Height:
50 µm
Step size:
0.5 µm
Step size:
5 µm
Step size:
1 µm
Final Polishing Step:
1 µm diamond paste
frames per second:
35 fps
frames per second:
46 fps
frames per second:
51 fps
Voltage:
30 kV
frames per second:
57 fps
EBSD Camera Binning:
1 x 1
Beam Intensity or current:
20
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.583
% points with CI>0.1:
0.874
% points with CI>0.1:
0.577
% points with CI>0.1:
0.764
% points with CI>0.1:
0.603
% points with CI>0.1:
0.604
% points with CI>0.1:
0.564
Basal PF Max:
2.6 MRD
name on specimen mount:
ZX30C_PSCd01
Total Fraction Less than 1º:
0.018 %
Unloaded strain:
7%
Alloy:
ZX30
Number of grains:
464
Total Fraction Less than 1º:
1.2 %
Average Diameter:
14.8 µm
Composition Zn content:
3.03 wt%
Number of grains:
430
Average Diameter:
16 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.013
Files
Gleeble (1)
Test Date:
8/25/22
Test Mode:
PSC
Testing Mode:
PSC
Initial height or thickness:
10.06 mm
Initial width:
14.96 mm
Initial length:
19.98 mm
Final height or thickness:
9.34 mm
Pre-deformation soak Temp:
350 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Post-deformation Soak Time:
0 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.577
% points with CI>0.1:
0.764
% points with CI>0.1:
0.874
% points with CI>0.1:
0.583
% points with CI>0.1:
0.564
% points with CI>0.1:
0.603
% points with CI>0.1:
0.604
Basal PF Max:
2.6 MRD
name on specimen mount:
ZX30C_PSCd01
Total Fraction Less than 1º:
0.018 %
Unloaded strain:
7%
Alloy:
ZX30
Number of grains:
464
Total Fraction Less than 1º:
1.2 %
Average Diameter:
14.8 µm
Composition Zn content:
3.03 wt%
Number of grains:
430
Average Diameter:
16 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.013
Files
Optical Microscopy (1)
Date:
8/29/2022
Measurements
% points with CI>0.1:
0.604
% points with CI>0.1:
0.603
% points with CI>0.1:
0.564
% points with CI>0.1:
0.583
% points with CI>0.1:
0.874
% points with CI>0.1:
0.577
% points with CI>0.1:
0.764
Basal PF Max:
2.6 MRD
name on specimen mount:
ZX30C_PSCd01
Total Fraction Less than 1º:
0.018 %
Unloaded strain:
7%
Alloy:
ZX30
Number of grains:
464
Total Fraction Less than 1º:
1.2 %
Average Diameter:
14.8 µm
Composition Zn content:
3.03 wt%
Number of grains:
430
Average Diameter:
16 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.013
Receive Samples (1)
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.764
% points with CI>0.1:
0.577
% points with CI>0.1:
0.874
% points with CI>0.1:
0.583
% points with CI>0.1:
0.564
% points with CI>0.1:
0.603
% points with CI>0.1:
0.604
Basal PF Max:
2.6 MRD
name on specimen mount:
ZX30C_PSCd01
Total Fraction Less than 1º:
0.018 %
Unloaded strain:
7%
Alloy:
ZX30
Number of grains:
464
Total Fraction Less than 1º:
1.2 %
Average Diameter:
14.8 µm
Composition Zn content:
3.03 wt%
Number of grains:
430
Average Diameter:
16 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.013
Files
Texture (1)
Measurements
% points with CI>0.1:
0.604
% points with CI>0.1:
0.603
% points with CI>0.1:
0.564
% points with CI>0.1:
0.583
% points with CI>0.1:
0.874
% points with CI>0.1:
0.577
% points with CI>0.1:
0.764
Basal PF Max:
2.6 MRD
name on specimen mount:
ZX30C_PSCd01
Total Fraction Less than 1º:
0.018 %
Unloaded strain:
7%
Alloy:
ZX30
Number of grains:
464
Total Fraction Less than 1º:
1.2 %
Average Diameter:
14.8 µm
Composition Zn content:
3.03 wt%
Number of grains:
430
Average Diameter:
16 µm
Composition Ca content:
0.096 wt%
Twin fraction:
0.013