Sample: ZX30C_lowT1pass_d04 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67402
EBSD (9)
Scan date:
12/21/22
Scan date:
11/7/22
Scan date:
2/9/24
SEM view field width:
550 µm
Scan Width:
1000 µm
Scan Width:
400 µm
Scan Width:
500 µm
Scan Height:
175 µm
Scan Height:
200 µm
Scan Height:
400 µm
Scan Width:
400 µm
Step size:
1 µm
Step size:
5 µm
Scan Height:
400 µm
frames per second:
20 fps
Step size:
1 µm
frames per second:
60 fps
EBSD Camera Binning:
1 x 1
Final Polishing Step:
1 µm diamond paste
EBSD Camera Binning:
1 x 1
Voltage:
30 kV
Background setting:
standard
Beam Intensity or current:
20
Grid type:
square
Final Polishing Step:
1 µm diamond paste
CI>0.1 after rescan:
0.637
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.572
% points with CI>0.1:
0.58
% points with CI>0.1:
0.49
% points with CI>0.1:
0.43
% points with CI>0.1:
0.42
% points with CI>0.1:
0.46
% points with CI>0.1:
0.47
% points with CI>0.1:
0.53
Alloy:
ZX30
Basal PF Max:
6.2 MRD
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
3 %
Composition Ca content:
0.096 wt%
Files
Gleeble (1)
Test Date:
10/28/22
Test Mode:
PSC
Testing Mode:
PSC
Initial height or thickness:
9.94 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
200 ºC
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.49
% points with CI>0.1:
0.42
% points with CI>0.1:
0.46
% points with CI>0.1:
0.47
% points with CI>0.1:
0.53
% points with CI>0.1:
0.58
% points with CI>0.1:
0.572
% points with CI>0.1:
0.43
Alloy:
ZX30
Basal PF Max:
6.2 MRD
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
3 %
Composition Ca content:
0.096 wt%
Files
Receive Samples (1)
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.572
% points with CI>0.1:
0.58
% points with CI>0.1:
0.53
% points with CI>0.1:
0.49
% points with CI>0.1:
0.43
% points with CI>0.1:
0.47
% points with CI>0.1:
0.46
% points with CI>0.1:
0.42
Alloy:
ZX30
Basal PF Max:
6.2 MRD
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
3 %
Composition Ca content:
0.096 wt%
Files
Texture (1)
Measurements
% points with CI>0.1:
0.49
% points with CI>0.1:
0.42
% points with CI>0.1:
0.43
% points with CI>0.1:
0.46
% points with CI>0.1:
0.572
% points with CI>0.1:
0.47
% points with CI>0.1:
0.53
% points with CI>0.1:
0.58
Alloy:
ZX30
Basal PF Max:
6.2 MRD
Unloaded strain:
100%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
3 %
Composition Ca content:
0.096 wt%