Sample: ZX30C_PSCd01_outside Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67403
EBSD (3)
Scan date:
1/16/23
Scan Width:
2000 µm
Scan Width:
1000 µm
Scan Height:
1000 µm
Step size:
2 µm
Step size:
5 µm
frames per second:
150 fps
EBSD Camera Binning:
1 x 1
Final Polishing Step:
1 µm diamond paste
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.766
% points with CI>0.1:
0.645
% points with CI>0.1:
0.63
Alloy:
ZX30
Basal PF Max:
2.5 MRD
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
81.2 %
Composition Ca content:
0.096 wt%
Number of grains:
965
Average Diameter:
32 µm
Files
Receive Samples (1)
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.766
% points with CI>0.1:
0.63
% points with CI>0.1:
0.645
Alloy:
ZX30
Basal PF Max:
2.5 MRD
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
81.2 %
Composition Ca content:
0.096 wt%
Number of grains:
965
Average Diameter:
32 µm
Files
SEM (1)
Date:
2/1/23
Mode:
BSE
Voltage:
20 kV
Measurements
% points with CI>0.1:
0.645
% points with CI>0.1:
0.63
% points with CI>0.1:
0.766
Alloy:
ZX30
Basal PF Max:
2.5 MRD
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
81.2 %
Composition Ca content:
0.096 wt%
Number of grains:
965
Average Diameter:
32 µm
Texture (1)
total area:
6 mm^2
Measurements
% points with CI>0.1:
0.645
% points with CI>0.1:
0.63
% points with CI>0.1:
0.766
Alloy:
ZX30
Basal PF Max:
2.5 MRD
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
81.2 %
Composition Ca content:
0.096 wt%
Number of grains:
965
Average Diameter:
32 µm
Files