Sample: AM40_2p5 Ungroup Processes
Last Updated: 1 month ago Owner: Tracy Berman ID: 67406
EBSD (6)
Settings
Region of Interest:
Edge
Region of Interest:
Center
Region of Interest:
Through
Date:
10/8/2015
Date:
No value
scan width:
500 µm
scan width:
335 µm
edge location with respect to image:
left
scan height:
335 µm
step size:
0.5 µm
scan width:
500 µm
scan height:
500 µm
edge location with respect to image:
left
scan width:
1250 µm
scan width:
280 µm
step size:
1 µm
step size:
0.5 µm
Voltage:
30 kV
step size:
0.6 µm
scan height:
750 µm
step size:
1 µm
Beam Intensity or current:
20
Voltage:
30 kV
scan height:
233 µm
Beam Intensity or current:
20
Voltage:
30 kV
step size:
0.5 µm
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.163 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
4.194 %
Plate Thickness:
2.5 mm
Standard deviation:
0.16 %
Standard deviation:
0.541 %
Standard deviation:
0.629 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
EPMA Data Collection (4)
Settings
Date:
42201
Date:
42163
Date:
42115
Region of interest:
near edge
Region of interest:
edge
Region of interest:
center
Elements Measured:
Al, Mg, Mn
Elements Measured:
Al, Mg, Zn, Mn
number of measurements made:
400
number of measurements made:
361
number of measurements made:
372
data start row:
1601
data start row:
1201
data start row:
1
data end row:
400
data end row:
1600
data end row:
1972
data end row:
361
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.163 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
4.194 %
Plate Thickness:
2.5 mm
Standard deviation:
0.629 %
Standard deviation:
0.541 %
Standard deviation:
0.16 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
EPMA WIRS Analysis (3)
Settings
Date:
10/26/2016
Region of Interest:
Near Edge
Region of Interest:
Edge
Region of Interest:
Center
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.163 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
4.194 %
Plate Thickness:
2.5 mm
Standard deviation:
0.629 %
Standard deviation:
0.541 %
Standard deviation:
0.16 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
Phase Fraction Analysis (3)
Settings
Region of Interest:
Edge
Region of Interest:
Near Edge
Region of Interest:
Center
Number of images analyzed:
20
Number of images analyzed:
15
Number of images analyzed:
12
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.163 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
4.194 %
Plate Thickness:
2.5 mm
Standard deviation:
0.16 %
Standard deviation:
0.629 %
Standard deviation:
0.541 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
Received As-Cast Plates (1)
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
4.194 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
1.163 %
Plate Thickness:
2.5 mm
Standard deviation:
0.16 %
Standard deviation:
0.541 %
Standard deviation:
0.629 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
SEM Imaging (3)
Settings
Date:
1/17/2016
Region of Interest:
Center
Region of Interest:
Edge
Region of Interest:
Near Edge
View Field Width:
50 µm
View Field Width:
200 µm
Imaging Mode:
SE
Voltage:
10 keV
Beam Intensity:
10
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
4.194 %
beta + Al-Mn phase fraction:
1.538 %
beta + Al-Mn phase fraction:
1.163 %
Plate Thickness:
2.5 mm
Standard deviation:
0.16 %
Standard deviation:
0.541 %
Standard deviation:
0.629 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %