Sample: AM40_5p0 Ungroup Processes
Last Updated: 1 month ago Owner: Tracy Berman ID: 67407
EBSD (11)
Settings
Region of Interest:
center
Region of Interest:
Center
Region of Interest:
Through
Region of Interest:
Edge
scan width:
335 µm
scan width:
675 µm
scan width:
500 µm
edge location with respect to image:
left
scan width:
337 µm
scan height:
335 µm
scan width:
300 µm
scan height:
337 µm
scan width:
500 µm
scan height:
500 µm
scan width:
337 µm
scan height:
675 µm
scan width:
2500 µm
scan height:
500 µm
scan height:
675 µm
scan height:
337 µm
step size:
0.5 µm
scan height:
300 µm
scan height:
750 µm
step size:
1 µm
step size:
1 µm
Voltage:
30 kV
step size:
0.5 µm
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.165 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.337 %
Plate Thickness:
5 mm
Standard deviation:
0.295 %
Standard deviation:
0.306 %
Standard deviation:
0.325 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
EPMA Data Collection (7)
Settings
Date:
42135
Date:
42170
Date:
42457
Date:
42115
Region of interest:
edge
Region of interest:
near edge
Region of interest:
center
Elements Measured:
Al, Mg, Mn
Elements Measured:
Mg, Al, Mn
number of measurements made:
400
number of measurements made:
262
data start row:
593
data start row:
1201
data start row:
1393
data start row:
1
data start row:
401
data start row:
993
data end row:
800
data end row:
992
data end row:
400
data end row:
1654
data end row:
1392
data end row:
1600
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.165 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.337 %
Plate Thickness:
5 mm
Standard deviation:
0.325 %
Standard deviation:
0.306 %
Standard deviation:
0.295 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
EPMA WIRS Analysis (3)
Settings
Date:
10/26/2016
Region of Interest:
Center
Region of Interest:
Edge
Region of Interest:
Near Edge
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.165 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.337 %
Plate Thickness:
5 mm
Standard deviation:
0.325 %
Standard deviation:
0.306 %
Standard deviation:
0.295 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
Phase Fraction Analysis (3)
Settings
Region of Interest:
Near Edge
Region of Interest:
Edge
Region of Interest:
Center
Number of images analyzed:
8
Number of images analyzed:
11
Number of images analyzed:
10
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.165 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.337 %
Plate Thickness:
5 mm
Standard deviation:
0.295 %
Standard deviation:
0.325 %
Standard deviation:
0.306 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files
Received As-Cast Plates (1)
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.337 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.165 %
Plate Thickness:
5 mm
Standard deviation:
0.295 %
Standard deviation:
0.306 %
Standard deviation:
0.325 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
SEM Imaging (3)
Settings
Date:
12/11/2015
Region of Interest:
Center
Region of Interest:
Edge
Region of Interest:
Near Edge
View Field Width:
200 µm
View Field Width:
50 µm
Imaging Mode:
SE
Voltage:
10 keV
Beam Intensity:
10
Measurements
Alloy Name:
AM40
beta + Al-Mn phase fraction:
1.337 %
beta + Al-Mn phase fraction:
1.328 %
beta + Al-Mn phase fraction:
1.165 %
Plate Thickness:
5 mm
Standard deviation:
0.295 %
Standard deviation:
0.306 %
Standard deviation:
0.325 %
Composition Al Content:
3.8 wt %
Composition Mn Content:
0.055 wt %
Composition Mg Content:
96.145 wt %
Files