Sample: AM60_2p5 Ungroup Processes
Last Updated: 1 month ago Owner: Tracy Berman ID: 67412
EBSD (12)
Settings
Region of Interest:
Through
Region of Interest:
Edge
Region of Interest:
edge
Region of Interest:
Center
scan width:
675 µm
edge location with respect to image:
left
scan width:
500 µm
edge location with respect to image:
top
scan width:
337 µm
scan width:
335 µm
scan width:
168 µm
scan width:
400 µm
scan height:
500 µm
scan width:
300 µm
scan height:
335 µm
scan height:
675 µm
scan height:
337 µm
scan width:
1250 µm
scan height:
300 µm
step size:
1 µm
scan height:
750 µm
step size:
0.5 µm
scan height:
413 µm
scan height:
168 µm
step size:
0.7 µm
Voltage:
30 kV
step size:
1 µm
step size:
0.4 µm
step size:
0.5 µm
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
3.022 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
4.506 %
Plate Thickness:
2.5 mm
Standard deviation:
0.316 %
Standard deviation:
0.26 %
Standard deviation:
0.367 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
EPMA Data Collection (11)
Settings
Date:
42076
Date:
41941
Date:
42101
Date:
42163
Date:
42170
Date:
41834
Region of interest:
near edge
Region of interest:
edge
Region of interest:
center
Elements Measured:
Al,Mg
Elements Measured:
Al, Mg, Zn, Mn
Elements Measured:
Al, Mg, Mn
number of measurements made:
280
number of measurements made:
400
number of measurements made:
228
data start row:
1201
data start row:
1
data start row:
401
data start row:
801
data start row:
1601
data end row:
2000
data end row:
1600
data end row:
1200
data end row:
680
data end row:
800
data end row:
400
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
3.022 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
4.506 %
Plate Thickness:
2.5 mm
Standard deviation:
0.367 %
Standard deviation:
0.26 %
Standard deviation:
0.316 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
EPMA WIRS Analysis (3)
Settings
Date:
10/26/2016
Region of Interest:
Edge
Region of Interest:
Center
Region of Interest:
Near Edge
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
3.022 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
4.506 %
Plate Thickness:
2.5 mm
Standard deviation:
0.367 %
Standard deviation:
0.26 %
Standard deviation:
0.316 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
Phase Fraction Analysis (3)
Settings
Region of Interest:
Near Edge
Region of Interest:
Edge
Region of Interest:
Center
Number of images analyzed:
10
Number of images analyzed:
11
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
3.022 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
4.506 %
Plate Thickness:
2.5 mm
Standard deviation:
0.316 %
Standard deviation:
0.367 %
Standard deviation:
0.26 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
Received As-Cast Plates (1)
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
4.506 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
3.022 %
Plate Thickness:
2.5 mm
Standard deviation:
0.316 %
Standard deviation:
0.26 %
Standard deviation:
0.367 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
SEM Imaging (3)
Settings
Date:
11/17/2015
Region of Interest:
Center
Region of Interest:
Edge
Region of Interest:
Near Edge
View Field Width:
50 µm
View Field Width:
200 µm
Imaging Mode:
SE
Voltage:
10 keV
Beam Intensity:
10
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
4.506 %
beta + Al-Mn phase fraction:
1.395 %
beta + Al-Mn phase fraction:
3.022 %
Plate Thickness:
2.5 mm
Standard deviation:
0.316 %
Standard deviation:
0.26 %
Standard deviation:
0.367 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files