Sample: AM60_5p0 Ungroup Processes
Last Updated: 1 month ago Owner: Tracy Berman ID: 67413
EBSD (12)
Settings
Region of Interest:
Edge
Region of Interest:
Through
Region of Interest:
Center
scan width:
1000 µm
scan width:
339 µm
scan width:
337 µm
scan width:
335 µm
scan width:
675 µm
scan width:
500 µm
edge location with respect to image:
left assumed
edge location with respect to image:
left
scan height:
335 µm
scan height:
600 µm
scan height:
500 µm
scan height:
337 µm
scan height:
1000 µm
scan width:
250 µm
scan width:
335 µm
scan width:
300 µm
scan width:
2500 µm
scan height:
250 µm
scan height:
335 µm
step size:
1 µm
scan height:
300 µm
step size:
0.5 µm
scan height:
750 µm
Voltage:
30 kV
step size:
0.6 µm
step size:
1 µm
step size:
0.5 µm
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.878 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.844 %
Plate Thickness:
5 mm
Standard deviation:
0.202 %
Standard deviation:
0.479 %
Standard deviation:
0.508 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
EPMA Data Collection (20)
Settings
Date:
41832
Date:
41816
Date:
42230
Date:
42229
Date:
42231
Date:
42094
Date:
41985
Date:
42095
Date:
42163
Date:
42185
Date:
42201
Date:
41964
Date:
41957
Date:
41822
Date:
41817
Region of interest:
near edge
Region of interest:
edge
Region of interest:
center
Elements Measured:
Al,Mg
Elements Measured:
Al,Mg,Zn,Mn
Elements Measured:
Al, Mg
Elements Measured:
Al, Mg, Mn
Elements Measured:
Al, Mg, Zn, Mn
Elements Measured:
Al Mg, Zn Mn
number of measurements made:
200
number of measurements made:
27
number of measurements made:
450
number of measurements made:
400
number of measurements made:
209
number of measurements made:
361
data start row:
801
data start row:
401
data start row:
1201
data start row:
1084
data start row:
681
data start row:
1484
data start row:
1
data start row:
41
data end row:
400
data end row:
890
data end row:
1483
data end row:
1200
data end row:
800
data end row:
1844
data end row:
450
data end row:
1227
data end row:
1009
data end row:
1080
data end row:
200
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.878 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.844 %
Plate Thickness:
5 mm
Standard deviation:
0.508 %
Standard deviation:
0.479 %
Standard deviation:
0.202 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
EPMA WIRS Analysis (3)
Settings
Date:
10/26/2016
Region of Interest:
Center
Region of Interest:
Edge
Region of Interest:
Near Edge
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.878 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.844 %
Plate Thickness:
5 mm
Standard deviation:
0.508 %
Standard deviation:
0.479 %
Standard deviation:
0.202 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
Phase Fraction Analysis (3)
Settings
Region of Interest:
Near Edge
Region of Interest:
Edge
Region of Interest:
Center
Number of images analyzed:
13
Number of images analyzed:
11
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.878 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.844 %
Plate Thickness:
5 mm
Standard deviation:
0.202 %
Standard deviation:
0.508 %
Standard deviation:
0.479 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files
Received As-Cast Plates (1)
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.844 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.878 %
Plate Thickness:
5 mm
Standard deviation:
0.202 %
Standard deviation:
0.479 %
Standard deviation:
0.508 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
SEM Imaging (3)
Settings
Date:
11/17/2015
Region of Interest:
Center
Region of Interest:
Near Edge
Region of Interest:
Edge
View Field Width:
50 µm
View Field Width:
200 µm
Imaging Mode:
SE
Voltage:
10 keV
Beam Intensity:
10
Measurements
Alloy Name:
AM60
beta + Al-Mn phase fraction:
1.844 %
beta + Al-Mn phase fraction:
1.213 %
beta + Al-Mn phase fraction:
1.878 %
Plate Thickness:
5 mm
Standard deviation:
0.202 %
Standard deviation:
0.479 %
Standard deviation:
0.508 %
Composition Al Content:
6.05 wt %
Composition Mn Content:
0.44 wt %
Composition Mg Content:
93.51 wt %
Files