View Sample

Sample: AM70_2p5 Ungroup Processes

EBSD (9)

Settings

Region of Interest:

Edge

Region of Interest:

Center

Region of Interest:

Through

edge location with respect to image:

left

scan width:

675 µm

scan width:

500 µm

scan width:

335 µm

scan width:

300 µm

scan height:

500 µm

scan height:

675 µm

step size:

1.5 µm

scan width:

1250 µm

scan width:

500 µm

scan height:

300 µm

scan height:

500 µm

Voltage:

30 kV

scan height:

335 µm

step size:

1 µm

step size:

0.7 µm

step size:

0.5 µm

scan height:

850 µm

Voltage:

30 kV

step size:

1 µm

Beam Intensity or current:

step size:

0.5 µm

Voltage:

30 kV

Beam Intensity or current:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Plate Thickness:

2.5 mm

Standard deviation:

0.468 %

Standard deviation:

0.896 %

Standard deviation:

1.533 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

See 5 more files......

EPMA Data Collection (5)

Settings

Date:

42201

Date:

42153

Region of interest:

near edge

Region of interest:

edge

Region of interest:

center

Elements Measured:

Al, Mg, Mn

number of measurements made:

361

number of measurements made:

400

data start row:

801

data start row:

723

data start row:

401

data start row:

362

data start row:

data end row:

1083

data end row:

800

data end row:

722

data end row:

400

data end row:

1200

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Plate Thickness:

2.5 mm

Standard deviation:

1.533 %

Standard deviation:

0.896 %

Standard deviation:

0.468 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

EPMA WIRS Analysis (3)

Settings

Date:

10/26/2016

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Plate Thickness:

2.5 mm

Standard deviation:

1.533 %

Standard deviation:

0.896 %

Standard deviation:

0.468 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

Phase Fraction Analysis (3)

Settings

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Number of images analyzed:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Plate Thickness:

2.5 mm

Standard deviation:

0.468 %

Standard deviation:

1.533 %

Standard deviation:

0.896 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

PhaseSeparationAlgorithm_Final.m

Received As-Cast Plates (1)

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

9.021 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

5.303 %

Plate Thickness:

2.5 mm

Standard deviation:

0.468 %

Standard deviation:

0.896 %

Standard deviation:

1.533 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

SEM Imaging (3)

Settings

Date:

11/5/2015

Region of Interest:

Center

Region of Interest:

Edge

Region of Interest:

Near Edge

View Field Width:

50 µm

View Field Width:

200 µm

Imaging Mode:

Voltage:

10 keV

Beam Intensity:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

9.021 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

5.303 %

Plate Thickness:

2.5 mm

Standard deviation:

0.468 %

Standard deviation:

0.896 %

Standard deviation:

1.533 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files