View Sample

Sample: AM70_5p0 Ungroup Processes

EBSD (9)

Settings

Region of Interest:

Center

Region of Interest:

Through

Region of Interest:

Edge

scan width:

335 µm

scan width:

500 µm

edge location with respect to image:

left

scan width:

600 µm

step size:

0.5 µm

scan width:

675 µm

scan width:

300 µm

step size:

0.5 µm

scan height:

600 µm

scan width:

335 µm

scan height:

675 µm

scan width:

2500 µm

Voltage:

30 kV

scan height:

335 µm

step size:

0.5 µm

scan height:

750 µm

Beam Intensity or current:

scan height:

335 µm

step size:

1 µm

step size:

0.75 µm

Voltage:

30 kV

scan height:

300 µm

step size:

1 µm

Voltage:

30 kV

step size:

0.5 µm

Beam Intensity or current:

Voltage:

30 kV

Beam Intensity or current:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

4.051 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

5.141 %

Plate Thickness:

5 mm

Standard deviation:

0.689 %

Standard deviation:

1.466 %

Standard deviation:

0.684 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

See 7 more files......

EPMA Data Collection (7)

Settings

Date:

42181

Date:

42185

Date:

42129

Region of interest:

near edge

Region of interest:

edge

Region of interest:

center

Elements Measured:

Al, Mg, Mn

Elements Measured:

Al, Mg, Zn

number of measurements made:

361

number of measurements made:

441

number of measurements made:

151

number of measurements made:

440

number of measurements made:

500

number of measurements made:

350

data start row:

942

data start row:

712

data start row:

501

data start row:

351

data end row:

500

data end row:

350

data end row:

862

data end row:

440

data end row:

1382

data end row:

941

data end row:

711

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

4.051 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

5.141 %

Plate Thickness:

5 mm

Standard deviation:

0.684 %

Standard deviation:

1.466 %

Standard deviation:

0.689 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

EPMA WIRS Analysis (3)

Settings

Region of Interest:

Center

Date:

10/26/2016

Region of Interest:

Near Edge

Region of Interest:

Edge

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

4.051 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

5.141 %

Plate Thickness:

5 mm

Standard deviation:

0.684 %

Standard deviation:

1.466 %

Standard deviation:

0.689 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

Phase Fraction Analysis (3)

Settings

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Number of images analyzed:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

4.051 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

5.141 %

Plate Thickness:

5 mm

Standard deviation:

0.689 %

Standard deviation:

0.684 %

Standard deviation:

1.466 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

PhaseSeparationAlgorithm_Final.m

Received As-Cast Plates (1)

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.141 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

4.051 %

Plate Thickness:

5 mm

Standard deviation:

0.689 %

Standard deviation:

1.466 %

Standard deviation:

0.684 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

SEM Imaging (3)

Settings

Date:

11/5/2015

Region of Interest:

Center

Region of Interest:

Edge

Region of Interest:

Near Edge

View Field Width:

200 µm

View Field Width:

50 µm

Imaging Mode:

Voltage:

10 keV

Beam Intensity:

Measurements

Alloy Name:

AM70

beta + Al-Mn phase fraction:

5.141 %

beta + Al-Mn phase fraction:

2.414 %

beta + Al-Mn phase fraction:

4.051 %

Plate Thickness:

5 mm

Standard deviation:

0.689 %

Standard deviation:

1.466 %

Standard deviation:

0.684 %

Composition Al Content:

7.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

92.51 wt %

Files

See 67 more files......