View Sample

Sample: Mg-11Al_2p5 Ungroup Processes

EBSD (3)

Settings

edge location with respect to image:

left

Voltage:

30 kV

Voltage:

30 kV

Beam Intensity or current:

Measurements

Alloy Name:

Mg-11Al

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Mean experimental Al content:

9.63 wt%

Mean experimental Al content:

5.42 wt%

Mean experimental Al content:

9.07 wt%

Plate Thickness:

2.5 mm

Standard deviation:

1.533 %

Standard deviation:

0.896 %

Standard deviation:

0.468 %

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Files

EPMA Data Collection (6)

Settings

Date:

42675

Date:

42436

Region of interest:

near edge

Region of interest:

edge

Region of interest:

center

Elements Measured:

Mg, Al, Zn, Mn

number of measurements made:

400

number of measurements made:

187

number of measurements made:

200

number of measurements made:

289

data start row:

1201

data start row:

401

data start row:

496

data start row:

201

data start row:

data end row:

489

data end row:

895

data end row:

200

data end row:

800

data end row:

400

data end row:

1387

Measurements

Alloy Name:

Mg-11Al

beta + Al-Mn phase fraction:

9.021 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

5.303 %

Mean experimental Al content:

5.42 wt%

Mean experimental Al content:

9.07 wt%

Mean experimental Al content:

9.63 wt%

Plate Thickness:

2.5 mm

Standard deviation:

0.468 %

Standard deviation:

1.533 %

Standard deviation:

0.896 %

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Files

EPMA WIRS Analysis (3)

Settings

Region of Interest:

Center

Region of Interest:

Edge

Region of Interest:

Near Edge

Measurements

Alloy Name:

Mg-11Al

beta + Al-Mn phase fraction:

5.303 %

beta + Al-Mn phase fraction:

3.338 %

beta + Al-Mn phase fraction:

9.021 %

Mean experimental Al content:

5.42 wt%

Mean experimental Al content:

9.07 wt%

Mean experimental Al content:

9.63 wt%

Plate Thickness:

2.5 mm

Standard deviation:

1.533 %

Standard deviation:

0.468 %

Standard deviation:

0.896 %

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Files

Forward Model Simulation (11)

Settings

Region of Interest:

center

Region of Interest:

edge

Region of Interest:

near edge

Simulated partition coefficient:

0.4 k_v

Simulated partition coefficient:

0.35 k_v

Simulated partition coefficient:

0.3 k_v

Simulated partition coefficient:

0.25 k_v

Simulated partition coefficient:

0.45 k_v

Mean simulated Al contentl:

4.07 wt%

Mean simulated Al contentl:

10.11 wt%

Mean simulated Al contentl:

9.15 wt%

Mean simulated Al contentl:

8.25 wt%

Mean simulated Al contentl:

5.64 wt%

Mean simulated Al contentl:

8.83 wt%

Mean simulated Al contentl:

5.15 wt%

Mean simulated Al contentl:

8.39 wt%

Mean simulated Al contentl:

9.14 wt%

Mean simulated Al contentl:

9.9 wt%

Mean simulated Al contentl:

10.09 wt%