Sample: Mg-11Al_5p0 Ungroup Processes
EBSD (3)
- Voltage:
- 30 kV
- edge location with respect to image:
- left
- Voltage:
- 30 kV
- Beam Intensity or current:
- 20
- Beam Intensity or current:
- 20
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 5.141 %
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 4.051 %
- Mean experimental Al content:
- 8.48 wt%
- Mean experimental Al content:
- 5.35 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.689 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.684 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
EPMA Data Collection (4)
- Date:
- 42675
- Date:
- 42426
- Date:
- 42436
- Region of interest:
- near edge
- Region of interest:
- center
- Elements Measured:
- Mg, Al, Zn, Mn
- number of measurements made:
- 400
- number of measurements made:
- 196
- number of measurements made:
- 225
- data start row:
- 990
- data start row:
- 1215
- data start row:
- 1296
- data start row:
- 1051
- data end row:
- 1439
- data end row:
- 1491
- data end row:
- 1450
- data end row:
- 1214
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 5.141 %
- beta + Al-Mn phase fraction:
- 4.051 %
- Mean experimental Al content:
- 5.35 wt%
- Mean experimental Al content:
- 8.48 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.684 %
- Standard deviation:
- 0.689 %
- Standard deviation:
- 1.466 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
EPMA WIRS Analysis (3)
- Region of Interest:
- Center
- Region of Interest:
- Edge
- Region of Interest:
- Near Edge
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 5.141 %
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 4.051 %
- Mean experimental Al content:
- 5.35 wt%
- Mean experimental Al content:
- 8.48 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.684 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.689 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
Forward Model Simulation (7)
- Region of Interest:
- near edge
- Region of Interest:
- center
- Simulated partition coefficient:
- 0.25 k_v
- Simulated partition coefficient:
- 0.4 k_v
- Simulated partition coefficient:
- 0.35 k_v
- Simulated partition coefficient:
- 0.3 k_v
- Mean simulated Al contentl:
- 4.02 wt%
- Mean simulated Al contentl:
- 5.4 wt%
- Mean simulated Al contentl:
- 5.21 wt%
- Mean simulated Al contentl:
- 9.29 wt%
- Mean simulated Al contentl:
- 7.37 wt%
- Mean simulated Al contentl:
- 8.45 wt%
- Mean simulated Al contentl:
- 8.87 wt%
- Least Squares difference simulation versus experiment:
- 1.76
- Least Squares difference simulation versus experiment:
- 0.07
- Least Squares difference simulation versus experiment:
- 0.06
- Least Squares difference simulation versus experiment:
- 5.68
- Least Squares difference simulation versus experiment:
- 5.69
- Least Squares difference simulation versus experiment:
- 5.06
- Least Squares difference simulation versus experiment:
- 5.24
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 4.051 %
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 5.141 %
- Mean experimental Al content:
- 5.35 wt%
- Mean experimental Al content:
- 8.48 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.689 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.684 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
Phase Fraction Analysis (3)
- Region of Interest:
- Center
- Region of Interest:
- Near Edge
- Region of Interest:
- Edge
- Number of images analyzed:
- 13
- Number of images analyzed:
- 11
- Number of images analyzed:
- 12
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 4.051 %
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 5.141 %
- Mean experimental Al content:
- 8.48 wt%
- Mean experimental Al content:
- 5.35 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.689 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.684 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
Received As-Cast Plates (1)
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 4.051 %
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 5.141 %
- Mean experimental Al content:
- 5.35 wt%
- Mean experimental Al content:
- 8.48 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.684 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.689 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
SEM Imaging (3)
- Date:
- 3/5/2016
- Region of Interest:
- Center
- Region of Interest:
- Edge
- Region of Interest:
- Near Edge
- View Field Width:
- 200 µm
- View Field Width:
- 50 µm
- Imaging Mode:
- SE
- Voltage:
- 10 keV
- Beam Intensity:
- 10
Measurements
- Alloy Name:
- Mg-11Al
- beta + Al-Mn phase fraction:
- 2.414 %
- beta + Al-Mn phase fraction:
- 5.141 %
- beta + Al-Mn phase fraction:
- 4.051 %
- Mean experimental Al content:
- 5.35 wt%
- Mean experimental Al content:
- 8.48 wt%
- Plate Thickness:
- 5 mm
- Standard deviation:
- 0.689 %
- Standard deviation:
- 1.466 %
- Standard deviation:
- 0.684 %
- Composition Al Content:
- 11.35 wt %
- Composition Mn Content:
- 0.1 wt %
- Composition Mg Content:
- 88.55 wt %
Files
- Mg_12Al_5p0_center2173-tif.hdr
- Mg_12Al_5p0_center2173.tif
- Mg_12Al_5p0_center2174-tif.hdr
- Mg_12Al_5p0_center2174.tif
- Mg_12Al_5p0_center2175-tif.hdr
- Mg_12Al_5p0_center2175.tif
- Mg_12Al_5p0_center2176-tif.hdr
- Mg_12Al_5p0_center2176.tif
- Mg_12Al_5p0_center2177-tif.hdr
- Mg_12Al_5p0_center2177.tif
- Mg_12Al_5p0_center2178-tif.hdr
- Mg_12Al_5p0_center2178.tif
- Mg_12Al_5p0_center2179-tif.hdr
- Mg_12Al_5p0_center2179.tif
- Mg_12Al_5p0_center2180-tif.hdr
- Mg_12Al_5p0_center2180.tif
- Mg_12Al_5p0_center2181-tif.hdr
- Mg_12Al_5p0_center2181.tif
- Mg_12Al_5p0_center2182-tif.hdr
- Mg_12Al_5p0_center2182.tif
- Mg_12Al_5p0_center2183-tif.hdr
- Mg_12Al_5p0_center2183.tif
- Mg_12Al_5p0_center2184-tif.hdr
- Mg_12Al_5p0_center2184.tif
- Mg_12Al_5p0_center2185-tif.hdr
- Mg_12Al_5p0_center2185.tif
- Mg_12Al_5p0_center2186-tif.hdr
- Mg_12Al_5p0_center2186.tif
- Mg_12Al_5p0_center2187-tif.hdr
- Mg_12Al_5p0_center2187.tif
- Mg_12Al_5p0_center2188-tif.hdr
- Mg_12Al_5p0_center2188.tif
- Mg_12Al_5p0_center2189-tif.hdr
- Mg_12Al_5p0_center2189.tif
- Mg_12Al_5p0_edge2203-tif.hdr
- Mg_12Al_5p0_edge2203.tif
- Mg_12Al_5p0_edge2204-tif.hdr
- Mg_12Al_5p0_edge2204.tif
- Mg_12Al_5p0_edge2205-tif.hdr
- Mg_12Al_5p0_edge2205.tif
- Mg_12Al_5p0_edge2206-tif.hdr
- Mg_12Al_5p0_edge2206.tif
- Mg_12Al_5p0_edge2207-tif.hdr
- Mg_12Al_5p0_edge2207.tif
- Mg_12Al_5p0_edge2208-tif.hdr
- Mg_12Al_5p0_edge2208.tif
- Mg_12Al_5p0_edge2209-tif.hdr
- Mg_12Al_5p0_edge2209.tif
- Mg_12Al_5p0_edge2210-tif.hdr
- Mg_12Al_5p0_edge2210.tif
- Mg_12Al_5p0_edge2211-tif.hdr
- Mg_12Al_5p0_edge2211.tif
- Mg_12Al_5p0_edge2212-tif.hdr
- Mg_12Al_5p0_edge2212.tif
- Mg_12Al_5p0_edge2213-tif.hdr
- Mg_12Al_5p0_edge2213.tif
- Mg_12Al_5p0_edge2214-tif.hdr
- Mg_12Al_5p0_edge2214.tif
- Mg_12Al_5p0_edge2215-tif.hdr
- Mg_12Al_5p0_edge2215.tif
- Mg_12Al_5p0_near_edge2190-tif.hdr
- Mg_12Al_5p0_near_edge2190.tif
- Mg_12Al_5p0_near_edge2191-tif.hdr
- Mg_12Al_5p0_near_edge2191.tif
- Mg_12Al_5p0_near_edge2192-tif.hdr
- Mg_12Al_5p0_near_edge2192.tif
- Mg_12Al_5p0_near_edge2193-tif.hdr
- Mg_12Al_5p0_near_edge2193.tif
- Mg_12Al_5p0_near_edge2194-tif.hdr
- Mg_12Al_5p0_near_edge2194.tif
- Mg_12Al_5p0_near_edge2195-tif.hdr
- Mg_12Al_5p0_near_edge2195.tif
- Mg_12Al_5p0_near_edge2196-tif.hdr
- Mg_12Al_5p0_near_edge2196.tif
- Mg_12Al_5p0_near_edge2197-tif.hdr
- Mg_12Al_5p0_near_edge2197.tif
- Mg_12Al_5p0_near_edge2198-tif.hdr
- Mg_12Al_5p0_near_edge2198.tif
- Mg_12Al_5p0_near_edge2199-tif.hdr
- Mg_12Al_5p0_near_edge2199.tif
- Mg_12Al_5p0_near_edge2200-tif.hdr
- Mg_12Al_5p0_near_edge2200.tif
- Mg_12Al_5p0_near_edge2201-tif.hdr
- Mg_12Al_5p0_near_edge2201.tif
- Mg_12Al_5p0_near_edge2202-tif.hdr
- Mg_12Al_5p0_near_edge2202.tif See 75 more files......