EPMA Data Collection (3)

Date:

42560

Region of interest:

near edge

Region of interest:

edge

Region of interest:

center

Elements Measured:

Mg, Al, Zn, Mn

number of measurements made:

50

number of measurements made:

49

data start row:

149

data start row:

248

data start row:

199

data end row:

296

data end row:

198

data end row:

247

Measurements

Alloy Name:

AM40

Plate Thickness:

5 mm

Composition Al Content:

3.8 wt %

Composition Mn Content:

0.055 wt %

Composition Mg Content:

96.145 wt %

Files

• berman_ST_MG-Al_run20160709.docx
• berman_ST_MG-Al_run20160709.xlsx

EPMA WIRS Analysis (3)

Date:

10/24/2016

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Measurements

Alloy Name:

AM40

Plate Thickness:

5 mm

Composition Al Content:

3.8 wt %

Composition Mn Content:

0.055 wt %

Composition Mg Content:

96.145 wt %

Files

• EPMA_Analysis.nb
• EPMA_Scans.xlsx
• Scheil_AM40-Ford_5p0_center_420C_120min.tif
  
• Scheil_AM40-Ford_5p0_center_420C_120min.xls
• Scheil_AM40-Ford_5p0_edge_420C_120min.tif
  
• Scheil_AM40-Ford_5p0_edge_420C_120min.xls
• Scheil_AM40-Ford_5p0_near edge_420C_120min.tif
  
• Scheil_AM40-Ford_5p0_near edge_420C_120min.xls

Received As-Cast Plates (1)

Measurements

Alloy Name:

AM40

Plate Thickness:

5 mm

Composition Al Content:

3.8 wt %

Composition Mn Content:

0.055 wt %

Composition Mg Content:

96.145 wt %

Solution Treatment (1)

Temperature:

420 ºC

Time:

2 h

Quench:

water

Measurements

Alloy Name:

AM40

Plate Thickness:

5 mm

Composition Al Content:

3.8 wt %

Composition Mn Content:

0.055 wt %

Composition Mg Content:

96.145 wt %