EPMA Data Collection (3)

Date:

42557

Region of interest:

edge

Region of interest:

near edge

Region of interest:

center

Elements Measured:

Mg, Al, Zn, Mn

number of measurements made:

49

number of measurements made:

50

data start row:

544

data start row:

445

data start row:

495

data end row:

592

data end row:

494

data end row:

543

Measurements

Alloy Name:

Mg-5Al

Plate Thickness:

5 mm

Composition Al Content:

4.8 wt %

Composition Mn Content:

0.09 wt %

Composition Mg Content:

95.11 wt %

Files

• berman_ST_MG-Al_run20160706.docx
• berman_ST_MG-Al_run20160706.xlsx

EPMA WIRS Analysis (3)

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Measurements

Alloy Name:

Mg-5Al

Plate Thickness:

5 mm

Composition Al Content:

4.8 wt %

Composition Mn Content:

0.09 wt %

Composition Mg Content:

95.11 wt %

Files

• EPMA_Analysis.nb
• EPMA_Scans.xlsx
• Scheil_Mg-5%Al_5p0_center_420C_120min.tif
  
• Scheil_Mg-5%Al_5p0_center_420C_120min.xls
• Scheil_Mg-5%Al_5p0_edge_420C_120min.tif
  
• Scheil_Mg-5%Al_5p0_edge_420C_120min.xls
• Scheil_Mg-5%Al_5p0_near edge_420C_120min.tif
  
• Scheil_Mg-5%Al_5p0_near edge_420C_120min.xls

Received As-Cast Plates (1)

Measurements

Alloy Name:

Mg-5Al

Plate Thickness:

5 mm

Composition Al Content:

4.8 wt %

Composition Mn Content:

0.09 wt %

Composition Mg Content:

95.11 wt %

Solution Treatment (1)

Temperature:

420 ºC

Time:

2 h

Quench:

water

Measurements

Alloy Name:

Mg-5Al

Plate Thickness:

5 mm

Composition Al Content:

4.8 wt %

Composition Mn Content:

0.09 wt %

Composition Mg Content:

95.11 wt %