EPMA Data Collection (5)

Date:

42557

Date:

42585

Region of interest:

edge

Region of interest:

near edge

Region of interest:

center

Elements Measured:

Mg, Al, Zn, Mn

number of measurements made:

50

number of measurements made:

49

data start row:

396

data start row:

692

data start row:

297

data start row:

643

data start row:

347

data end row:

740

data end row:

444

data end row:

346

data end row:

691

data end row:

395

Measurements

Alloy Name:

AM60

Plate Thickness:

2.5 mm

Composition Al Content:

6.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

93.51 wt %

Files

• berman_ST_MG_AL_run20160803.docx
• berman_ST_MG_AL_run20160803.xlsx
• berman_ST_MG-Al_run20160706.docx
• berman_ST_MG-Al_run20160706.xlsx

EPMA WIRS Analysis (3)

Date:

10/24/2016

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Measurements

Alloy Name:

AM60

Plate Thickness:

2.5 mm

Composition Al Content:

6.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

93.51 wt %

Files

• EPMA_Analysis.nb
• EPMA_Scans.xlsx
• Scheil_AM60-Ford_2p5_center_420C_120min.tif
  
• Scheil_AM60-Ford_2p5_center_420C_120min.xls
• Scheil_AM60-Ford_2p5_edge_420C_120min.tif
  
• Scheil_AM60-Ford_2p5_edge_420C_120min.xls
• Scheil_AM60-Ford_2p5_near edge_420C_120min.tif
  
• Scheil_AM60-Ford_2p5_near edge_420C_120min.xls

Received As-Cast Plates (1)

Measurements

Alloy Name:

AM60

Plate Thickness:

2.5 mm

Composition Al Content:

6.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

93.51 wt %

Solution Treatment (1)

Temperature:

420 ºC

Time:

2 h

Quench:

water

Measurements

Alloy Name:

AM60

Plate Thickness:

2.5 mm

Composition Al Content:

6.05 wt %

Composition Mn Content:

0.44 wt %

Composition Mg Content:

93.51 wt %