Sample: AM60_5p0 ST Ungroup Processes
EPMA Data Collection (7)
- Date:
- 42293
- Date:
- 42655
- Date:
- 42585
- Date:
- 42557
- Region of interest:
- near edge
- Region of interest:
- center
- Region of interest:
- edge
- Elements Measured:
- Mg, Al, Zn, Mn
- number of measurements made:
- 49
- number of measurements made:
- 50
- data start row:
- 445
- data start row:
- 451
- data start row:
- 791
- data start row:
- 495
- data start row:
- 544
- data start row:
- 840
- data end row:
- 494
- data end row:
- 592
- data end row:
- 839
- data end row:
- 543
- data end row:
- 500
- data end row:
- 888
Measurements
- Alloy Name:
- AM60
- Plate Thickness:
- 5 mm
- Composition Al Content:
- 6.05 wt %
- Composition Mn Content:
- 0.44 wt %
- Composition Mg Content:
- 93.51 wt %
Files
EPMA WIRS Analysis (3)
- Date:
- 10/24/2016
- Region of Interest:
- Near Edge
- Region of Interest:
- Edge
- Region of Interest:
- Center
Measurements
- Alloy Name:
- AM60
- Plate Thickness:
- 5 mm
- Composition Al Content:
- 6.05 wt %
- Composition Mn Content:
- 0.44 wt %
- Composition Mg Content:
- 93.51 wt %
Files
Received As-Cast Plates (1)
Measurements
- Alloy Name:
- AM60
- Plate Thickness:
- 5 mm
- Composition Al Content:
- 6.05 wt %
- Composition Mn Content:
- 0.44 wt %
- Composition Mg Content:
- 93.51 wt %
Solution Treatment (1)
- Temperature:
- 420 ºC
- Time:
- 2 h
- Quench:
- water
Measurements
- Alloy Name:
- AM60
- Plate Thickness:
- 5 mm
- Composition Al Content:
- 6.05 wt %
- Composition Mn Content:
- 0.44 wt %
- Composition Mg Content:
- 93.51 wt %