EPMA Data Collection (3)

Date:

42557

Region of interest:

edge

Region of interest:

near edge

Region of interest:

center

Elements Measured:

Mg, Al, Zn, Mn

number of measurements made:

49

number of measurements made:

50

data start row:

988

data start row:

889

data start row:

939

data end row:

1036

data end row:

938

data end row:

987

Measurements

Alloy Name:

Mg-11Al

Plate Thickness:

2.5 mm

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Files

• berman_ST_MG-Al_run20160706.docx
• berman_ST_MG-Al_run20160706.xlsx

EPMA WIRS Analysis (3)

Region of Interest:

Near Edge

Region of Interest:

Edge

Region of Interest:

Center

Measurements

Alloy Name:

Mg-11Al

Plate Thickness:

2.5 mm

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Files

• EPMA_Analysis.nb
• EPMA_Scans.xlsx
• Scheil_Mg-12%Al_2p5_center_420C_120min.tif
  
• Scheil_Mg-12%Al_2p5_center_420C_120min.xls
• Scheil_Mg-12%Al_2p5_edge_420C_120min.tif
  
• Scheil_Mg-12%Al_2p5_edge_420C_120min.xls
• Scheil_Mg-12%Al_2p5_near edge_420C_120min.tif
  
• Scheil_Mg-12%Al_2p5_near edge_420C_120min.xls

Received As-Cast Plates (1)

Measurements

Alloy Name:

Mg-11Al

Plate Thickness:

2.5 mm

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %

Solution Treatment (1)

Temperature:

420 ºC

Time:

2 h

Quench:

water

Measurements

Alloy Name:

Mg-11Al

Plate Thickness:

2.5 mm

Composition Al Content:

11.35 wt %

Composition Mn Content:

0.1 wt %

Composition Mg Content:

88.55 wt %