Sample: ZX10_d46 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67489
EBSD (5)
Scan date:
7/16/2021
Scan date:
7/19/2021
Scan date:
7/14/2021
Scan Width:
800 µm
Scan Width:
2000 µm
Scan Width:
200 µm
Scan Height:
800 µm
Scan Height:
200 µm
Step size:
3 µm
Step size:
1 µm
Step size:
0.33 µm
frames per second:
33 fps
frames per second:
32 fps
frames per second:
38 fps
Sample orientation vertical direction:
RD
Working Distance:
20 mm
Quick grain diameter - OM:
2 µm
Sample orientation vertical direction:
RD
Voltage:
30 kV
Voltage:
30 kV
Beam Intensity or current:
20
Total Grains:
18.3
Beam Intensity or current:
20
Sample orientation vertical direction:
RD
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files
Gleeble (1)
Test date:
7/12/2021
Start Length:
20.19 mm
Start Width:
15.2 mm
Start Thickness:
9.89 mm
Final Thickness:
1.83 mm
Deformations:
10
Program Strain Type:
TRUE
Pre-deformation Soak Temp:
350 ºC
Rate to Temp:
5 ºC/s
Pre-deformation Soak Time:
600 s
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.2
Stage One - Temp during Deformations:
350 ºC
Stage One - interpass anneal Temp:
350 ºC
Stage One - interpass anneal Time:
600 s
Stage Two - Number of passes:
0
Quench Duration:
30 s
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files
Grain Analysis (1)
Analysis Date:
11/12/2021
Input file:
ZX10_D46_scan20210714.osc
Used in histogram:
Y
Rough starting grain size:
2.2 mm
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files
Optical Microscopy (10)
Date:
7/14/2021
Objective Mag:
100
Objective Mag:
50
Objective Mag:
20
Objective Mag:
10
Objective Mag:
5
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files
Receive Samples (1)
Receipt Date:
11/2/2018
Source:
University of Florida
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files
Texture (1)
Basal PF Max:
6.4 MRD
Measurements
Alloy:
ZX10
Total grains:
1346
Composition Zn content:
1 wt%
Mean diameter:
19.3 µm
Composition Ca content:
0.1 wt%
Median diameter:
12.6 µm
Max diameter:
85 µm
Files