Sample: ZX10-S2 Ungroup Processes
Last Updated: 2 days ago Owner: Tracy Berman ID: 67493
Beamrun_Metadata (1)
Experiment Date:
9/27/2021
Beamrun:
2021-3
Beamrun Directory:
 bucsek-2800-f
Preprocess Threshold:
200
Synchrotron:
CHESS
Beamline:
FAST
Experiment Type:
Recrystallization
Heating Fixture:
RAMS2 - Halogen Bulb Furnace
X-Ray Modality:
Monochromatic
X-Ray Energy:
55.618 keV
Beam Width:
2 mm
Beam Height:
0.1 mm
Number of beam layers:
1
Exposure Time:
0.25 s
X-Ray Technique:
ff-HEDM
Detector:
Dexela
Calibrant 1:
CeO2
Calibrant 1 Sample ID:
ceo2-01
Calibrant 2:
multiruby
Calibrant 2 Sample ID:
1
Calibrant 2 Pre-Processing Threshold:
25
Reconstruction Software:
HEXRD
Reconstruction Software Version:
0.8.3
FindOrientations Theshold:
100
FindOrientations bin frames:
1
FindOrientations active hkls:
0,3,4,5
FindOrientations hkl_seeds:
0,3
FindOrientations fiber step:
0.5 deg
FindOrientations seed search method:
blob_log
FindOrientations blob_log min_sigma:
0.5
FindOrientations blob_log max_sigma:
5
FindOrientations blob_log num_sigma:
10
FindOrientations blob_log threshold:
0.1
FindOrientations blob_log overlap:
0.1
FindOrientations On-Map Threshold:
1
FindOrientations ome tol:
0.25 deg
FindOrientations eta tol:
0.25 deg
FindOrientations eta mask:
5 deg
FindOrientations Clustering Radius:
1 deg
FindOrientations Clustering Thresh:
0.9
FitGrains number polar px grid divisions:
4
FitGrains threshold:
25
FitGrains tth tol:
0.25,0.20 deg
FitGrains eta tol:
1,0.5 deg
FitGrains ome tol:
1,0.5 deg
FitGrains refit tol:
3,1 deg
FitGrains tth max:
TRUE deg or T/F
Measurements
Material Name:
ZX10
Material Chemistry:
Mg-1wt%Zn-0.1Ca
Material Class:
Metal
Phases:
P63/mmc
Files
Far-Field HEDM Step (12)
Recrystallization Step:
04
Recrystallization Step:
07
Recrystallization Step:
08
Recrystallization Step:
06
Recrystallization Step:
09
Recrystallization Step:
05
Recrystallization Step:
10
Recrystallization Step:
11
Recrystallization Step:
03
Recrystallization Step:
12
Recrystallization Step:
02
Recrystallization Step:
01
Start Scan Number:
198
Start Scan Number:
173
Start Scan Number:
189
Start Scan Number:
227
Start Scan Number:
182
Start Scan Number:
176
Start Scan Number:
86
Start Scan Number:
167
Start Scan Number:
164
Start Scan Number:
131
Start Scan Number:
112
Start Scan Number:
119
Recrystallization Temperature:
290 °C
Recrystallization Temperature:
335 °C
Recrystallization Time:
63 min
Recrystallization Time:
38 min
Recrystallization Time:
197 min
Recrystallization Time:
230 min
Recrystallization Time:
125 min
Recrystallization Time:
263 min
Recrystallization Time:
43 min
Recrystallization Time:
353 min
Recrystallization Time:
54 min
Recrystallization Time:
48 min
Recrystallization Time:
41 min
Recrystallization Time:
46 min
Measurements
Material Name:
ZX10
Material Chemistry:
Mg-1wt%Zn-0.1Ca
Material Class:
Metal
Phases:
P63/mmc
Files