Sample: CCV1-5.0a-08-au Ungroup Processes
Last Updated: 3 days ago Owner: Megan Trombley ID: 67515
Defect Size (1)
From:
Fractography
Number of Defects Measured:
27
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Files
Fractography (1)
From:
Ultrasonic Fatigue Testing
SEM Lab:
Gerstacker
SEM Machine:
Tescan MIRA3
Beam Voltage:
5 kV
Beam Intensity:
10
Image Date:
7/14/2020
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Processing Conditions (1)
Gauge Size:
5.0 mm
Geometry:
a - nominal
Source Lab:
NRL
Machine:
Concept Laser M2
Source Powder:
Concept Laser CL 20ES 316L
Build Orientation:
Vertical
Laser Type:
400W Fiber Laser (λ=1070 nm)
Laser Power Used:
370 W
Power Percentage:
92.5 %
Layer Thickness:
25 um
Velocity:
900 mm/s
Laser Spot Size:
160 um
Scan Pattern:
Infill/Contour
Scan Strategies:
Directional
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
RFL Analysis (1)
From:
Ultrasonic Fatigue Testing
Distribution:
Weibull
Constraint:
No
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Files
Sample Conditions (1)
From:
Processing Conditions
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Surface Roughness (1)
From:
Sample Conditions
Date:
2/10/2022
Source:
Megan
Equipment:
Keyence
Type:
Optical
Number of Measurements:
3
Ls Measurement:
None
Lc Measurement:
None
Lf Measurement:
None
End Effect Correction:
ON
Double Gaussian:
OFF
Surface Roughness Filter:
Gaussian
S-filter:
None
L-filter:
None
Avg Area Size [um^2]:
1066036.33
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Ultrasonic Fatigue Testing (1)
From:
Sample Conditions
Test Date:
2/4/2020
Control Unit:
3
R Ratio:
-1
Pulse:
200 ms
Pause:
3000 ms
Amplifiers:
4
Pre Adjust Setting:
25.0
Power Control Setting:
3
Max Stress:
120 MPa
Max Strain:
727
Test Amplitude:
390
Measurements
Average Area:
338.248 um^2
Avg Ra [um]:
3.62
Mean:
89.5 MPa
Resonant Frequency:
19.385 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
16.761 um
Avg Rz [um]:
23.30
Condition:
a - As-Built
Number of Cycles:
1.20E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
146.225 um
Avg RzJIS [um]:
16.57
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Avg Rp [um]:
10.38
Avg Rv [um]:
12.93
Avg Rc [um]:
14.42
Avg Rt [um]:
23.30
Avg Rq [um]:
4.61
Avg Rsk:
-0.13
Avg Rku:
3.44
Avg RSm [um]:
154.97
Avg Rdq:
0.58
Avg Sa [um]:
3.93
Avg Sz [um]:
37.05
Avg Sq [um]:
5.00
Avg Ssk:
0.11
Avg Sku:
3.21
Avg Sp [um]:
19.47
Avg Sv [um]:
17.58
Files