Sample: CCV1-5.0a-09-au Ungroup Processes
Last Updated: 3 days ago Owner: Megan Trombley ID: 67516
Defect Size (1)
From:
Fractography
Number of Defects Measured:
70
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Files
Fractography (1)
From:
Ultrasonic Fatigue Testing
SEM Lab:
Gerstacker
SEM Machine:
Tescan MIRA3
Beam Voltage:
5 kV
Beam Intensity:
10
Image Date:
7/24/2020
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Processing Conditions (1)
Gauge Size:
5.0 mm
Geometry:
a - nominal
Source Lab:
NRL
Machine:
Concept Laser M2
Source Powder:
Concept Laser CL 20ES 316L
Build Orientation:
Vertical
Laser Type:
400W Fiber Laser (λ=1070 nm)
Laser Power Used:
370 W
Power Percentage:
92.5 %
Layer Thickness:
25 um
Velocity:
900 mm/s
Laser Spot Size:
160 um
Scan Pattern:
Infill/Contour
Scan Strategies:
Directional
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
RFL Analysis (1)
From:
Ultrasonic Fatigue Testing
Distribution:
Weibull
Constraint:
No
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Files
Sample Conditions (1)
From:
Processing Conditions
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Ultrasonic Fatigue Testing (1)
From:
Sample Conditions
Test Date:
2/18/2020
Control Unit:
3
R Ratio:
-1
Pulse:
200 ms
Pause:
3000 ms
Amplifiers:
4
Pre Adjust Setting:
25.0
Power Control Setting:
3
Max Stress:
120 MPa
Max Strain:
727
Test Amplitude:
690
Measurements
Average Area:
144.959 um^2
Mean:
89.5 MPa
Resonant Frequency:
19.453 kHz
Sample Geometry:
5.0mm, nominal
Average Diameter:
15.193 um
Condition:
a - As-Built
Number of Cycles:
1.60E+6
Standard Deviation:
5.7 MPa
Average Edge Distance:
59.612 um
Runout or Failure?:
Failure
Tests:
u - Ultrasonic Fatigue
Files