Sample: CCV2-5.0a-02-ar Ungroup Processes
Axial Residual Stress Depth (3)
- From:
- Sample Conditions
- Date:
- 2/17/2022
- Supplier:
- Proto Manufacturing Inc
- Method:
- XRD
- Instrument:
- LXRD 13115
- Target:
- Mn K-α (2.1031 Å)
- X-Ray Elastic Constant:
- 139 GPa
- Young's Modulus:
- 174 GPa
- Poisson Ratio:
- 0.25
- Crystallographic Plane:
- {311}
- Bragg Angle, 2θ:
- 152.8 degrees
- Angular position:
- 0 deg
- Angular position:
- 120 deg
- Angular position:
- 240 deg
Measurements
- Depth of measurement 1:
- 0 mm
- Measured stress at angular position 0 deg:
- +271 ± 15 MPa
- Sample Geometry:
- 5.0mm, nominal
- As-measured stress 1:
- +272 ± 15 MPa
- As-measured stress 1:
- +339 ± 15 MPa
- As-measured stress 1:
- +266 ± 8 MPa
- Condition:
- a - As-Built
- Measured stress at angular position 60 deg:
- +340 ± 15 MPa
- Gradient corrected stress 1:
- +257 ± 16 MPa
- Gradient corrected stress 1:
- +322 ± 15 MPa
- Gradient corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 120 deg:
- +339 ± 15 MPa
- Tests:
- r - Residual stress
- Gradient & depth corrected stress 1:
- +257 ± 16 MPa
- Gradient & depth corrected stress 1:
- +322 ± 15 MPa
- Gradient & depth corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 180 deg:
- +333 ± 15 MPa
- Measurements:
- Residual stress depth, Proto
- Depth of measurement 2:
- 0.1289 mm
- Depth of measurement 2:
- 0.1385 mm
- Depth of measurement 2:
- 0.1297 mm
- Measured stress at angular position 240 deg:
- +266 ± 8 MPa
- As-measured stress 2:
- +583 ± 33 MPa
- As-measured stress 2:
- +729 ± 43 MPa
- As-measured stress 2:
- +653 ± 32 MPa
- Measured stress at angular position 300 deg:
- +186 ± 13 MPa
- Gradient corrected stress 2:
- +574 ± 34 MPa
- Gradient corrected stress 2:
- +723 ± 43 MPa
- Gradient corrected stress 2:
- +647 ± 33 MPa
- Gradient & depth corrected stress 2:
- +531 ± 34 MPa
- Gradient & depth corrected stress 2:
- +665 ± 43 MPa
- Gradient & depth corrected stress 2:
- +601 ± 33 MPa
- Depth of measurement 3:
- 0.1968 mm
- Depth of measurement 3:
- 0.2107 mm
- Depth of measurement 3:
- 0.2040 mm
- As-measured stress 3:
- +663 ± 24 MPa
- As-measured stress 3:
- +748 ± 48 MPa
- As-measured stress 3:
- +635 ± 31 MPa
- Gradient corrected stress 3:
- +656 ± 24 MPa
- Gradient corrected stress 3:
- +747 ± 45 MPa
- Gradient corrected stress 3:
- +637 ± 30 MPa
- Gradient & depth corrected stress 3:
- +580 ± 24 MPa
- Gradient & depth corrected stress 3:
- +646 ± 45 MPa
- Gradient & depth corrected stress 3:
- +552 ± 30 MPa
Files
Axial Residual Stress Surface (1)
- From:
- Sample Conditions
- Date:
- 2/17/2022
- Supplier:
- Proto Manufacturing Inc
- Method:
- XRD
- Instrument:
- LXRD 13115
Measurements
- Depth of measurement 1:
- 0 mm
- Measured stress at angular position 0 deg:
- +271 ± 15 MPa
- Sample Geometry:
- 5.0mm, nominal
- As-measured stress 1:
- +272 ± 15 MPa
- As-measured stress 1:
- +339 ± 15 MPa
- As-measured stress 1:
- +266 ± 8 MPa
- Condition:
- a - As-Built
- Measured stress at angular position 60 deg:
- +340 ± 15 MPa
- Gradient corrected stress 1:
- +257 ± 16 MPa
- Gradient corrected stress 1:
- +322 ± 15 MPa
- Gradient corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 120 deg:
- +339 ± 15 MPa
- Tests:
- r - Residual stress
- Gradient & depth corrected stress 1:
- +257 ± 16 MPa
- Gradient & depth corrected stress 1:
- +322 ± 15 MPa
- Gradient & depth corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 180 deg:
- +333 ± 15 MPa
- Measurements:
- Residual stress depth, Proto
- Depth of measurement 2:
- 0.1289 mm
- Depth of measurement 2:
- 0.1385 mm
- Depth of measurement 2:
- 0.1297 mm
- Measured stress at angular position 240 deg:
- +266 ± 8 MPa
- As-measured stress 2:
- +583 ± 33 MPa
- As-measured stress 2:
- +729 ± 43 MPa
- As-measured stress 2:
- +653 ± 32 MPa
- Measured stress at angular position 300 deg:
- +186 ± 13 MPa
- Gradient corrected stress 2:
- +574 ± 34 MPa
- Gradient corrected stress 2:
- +723 ± 43 MPa
- Gradient corrected stress 2:
- +647 ± 33 MPa
- Gradient & depth corrected stress 2:
- +531 ± 34 MPa
- Gradient & depth corrected stress 2:
- +665 ± 43 MPa
- Gradient & depth corrected stress 2:
- +601 ± 33 MPa
- Depth of measurement 3:
- 0.1968 mm
- Depth of measurement 3:
- 0.2107 mm
- Depth of measurement 3:
- 0.2040 mm
- As-measured stress 3:
- +663 ± 24 MPa
- As-measured stress 3:
- +748 ± 48 MPa
- As-measured stress 3:
- +635 ± 31 MPa
- Gradient corrected stress 3:
- +656 ± 24 MPa
- Gradient corrected stress 3:
- +747 ± 45 MPa
- Gradient corrected stress 3:
- +637 ± 30 MPa
- Gradient & depth corrected stress 3:
- +580 ± 24 MPa
- Gradient & depth corrected stress 3:
- +646 ± 45 MPa
- Gradient & depth corrected stress 3:
- +552 ± 30 MPa
Files
Processing Conditions (1)
- Gauge Size:
- 5.0 mm
- Geometry:
- a - nominal
- Source Lab:
- NRL
- Machine:
- Concept Laser M2
- Source Powder:
- Concept Laser CL 20ES 316L
- Build Orientation:
- Vertical
- Laser Type:
- 400W Fiber Laser (λ=1070 nm)
- Laser Power Used:
- 370 W
- Power Percentage:
- 92.5 %
- Layer Thickness:
- 25 um
- Velocity:
- 900 mm/s
- Laser Spot Size:
- 160 um
- Scan Pattern:
- Infill/Contour
- Scan Strategies:
- Directional
Measurements
- Depth of measurement 1:
- 0 mm
- Measured stress at angular position 0 deg:
- +271 ± 15 MPa
- Sample Geometry:
- 5.0mm, nominal
- As-measured stress 1:
- +272 ± 15 MPa
- As-measured stress 1:
- +339 ± 15 MPa
- As-measured stress 1:
- +266 ± 8 MPa
- Condition:
- a - As-Built
- Measured stress at angular position 60 deg:
- +340 ± 15 MPa
- Gradient corrected stress 1:
- +257 ± 16 MPa
- Gradient corrected stress 1:
- +322 ± 15 MPa
- Gradient corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 120 deg:
- +339 ± 15 MPa
- Tests:
- r - Residual stress
- Gradient & depth corrected stress 1:
- +257 ± 16 MPa
- Gradient & depth corrected stress 1:
- +322 ± 15 MPa
- Gradient & depth corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 180 deg:
- +333 ± 15 MPa
- Measurements:
- Residual stress depth, Proto
- Depth of measurement 2:
- 0.1289 mm
- Depth of measurement 2:
- 0.1385 mm
- Depth of measurement 2:
- 0.1297 mm
- Measured stress at angular position 240 deg:
- +266 ± 8 MPa
- As-measured stress 2:
- +583 ± 33 MPa
- As-measured stress 2:
- +729 ± 43 MPa
- As-measured stress 2:
- +653 ± 32 MPa
- Measured stress at angular position 300 deg:
- +186 ± 13 MPa
- Gradient corrected stress 2:
- +574 ± 34 MPa
- Gradient corrected stress 2:
- +723 ± 43 MPa
- Gradient corrected stress 2:
- +647 ± 33 MPa
- Gradient & depth corrected stress 2:
- +531 ± 34 MPa
- Gradient & depth corrected stress 2:
- +665 ± 43 MPa
- Gradient & depth corrected stress 2:
- +601 ± 33 MPa
- Depth of measurement 3:
- 0.1968 mm
- Depth of measurement 3:
- 0.2107 mm
- Depth of measurement 3:
- 0.2040 mm
- As-measured stress 3:
- +663 ± 24 MPa
- As-measured stress 3:
- +748 ± 48 MPa
- As-measured stress 3:
- +635 ± 31 MPa
- Gradient corrected stress 3:
- +656 ± 24 MPa
- Gradient corrected stress 3:
- +747 ± 45 MPa
- Gradient corrected stress 3:
- +637 ± 30 MPa
- Gradient & depth corrected stress 3:
- +580 ± 24 MPa
- Gradient & depth corrected stress 3:
- +646 ± 45 MPa
- Gradient & depth corrected stress 3:
- +552 ± 30 MPa
Sample Conditions (1)
- From:
- Processing Conditions
Measurements
- Depth of measurement 1:
- 0 mm
- Measured stress at angular position 0 deg:
- +271 ± 15 MPa
- Sample Geometry:
- 5.0mm, nominal
- As-measured stress 1:
- +272 ± 15 MPa
- As-measured stress 1:
- +339 ± 15 MPa
- As-measured stress 1:
- +266 ± 8 MPa
- Condition:
- a - As-Built
- Measured stress at angular position 60 deg:
- +340 ± 15 MPa
- Gradient corrected stress 1:
- +257 ± 16 MPa
- Gradient corrected stress 1:
- +322 ± 15 MPa
- Gradient corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 120 deg:
- +339 ± 15 MPa
- Tests:
- r - Residual stress
- Gradient & depth corrected stress 1:
- +257 ± 16 MPa
- Gradient & depth corrected stress 1:
- +322 ± 15 MPa
- Gradient & depth corrected stress 1:
- +249 ± 8 MPa
- Measured stress at angular position 180 deg:
- +333 ± 15 MPa
- Measurements:
- Residual stress depth, Proto
- Depth of measurement 2:
- 0.1289 mm
- Depth of measurement 2:
- 0.1385 mm
- Depth of measurement 2:
- 0.1297 mm
- Measured stress at angular position 240 deg:
- +266 ± 8 MPa
- As-measured stress 2:
- +583 ± 33 MPa
- As-measured stress 2:
- +729 ± 43 MPa
- As-measured stress 2:
- +653 ± 32 MPa
- Measured stress at angular position 300 deg:
- +186 ± 13 MPa
- Gradient corrected stress 2:
- +574 ± 34 MPa
- Gradient corrected stress 2:
- +723 ± 43 MPa
- Gradient corrected stress 2:
- +647 ± 33 MPa
- Gradient & depth corrected stress 2:
- +531 ± 34 MPa
- Gradient & depth corrected stress 2:
- +665 ± 43 MPa
- Gradient & depth corrected stress 2:
- +601 ± 33 MPa
- Depth of measurement 3:
- 0.1968 mm
- Depth of measurement 3:
- 0.2107 mm
- Depth of measurement 3:
- 0.2040 mm
- As-measured stress 3:
- +663 ± 24 MPa
- As-measured stress 3:
- +748 ± 48 MPa
- As-measured stress 3:
- +635 ± 31 MPa
- Gradient corrected stress 3:
- +656 ± 24 MPa
- Gradient corrected stress 3:
- +747 ± 45 MPa
- Gradient corrected stress 3:
- +637 ± 30 MPa
- Gradient & depth corrected stress 3:
- +580 ± 24 MPa
- Gradient & depth corrected stress 3:
- +646 ± 45 MPa
- Gradient & depth corrected stress 3:
- +552 ± 30 MPa