Sample: Mg1Y_UM173B_177C2month_Foil1 Ungroup Processes

Alloy Received (1)

Settings

Provider:

Canmet

Receive Date:

2022 May

Measurements

Alloy:

Mg1Y

Composition Y Content:

1 wt%

Casting Billet:

N2134

Extrusion Bar Number:

UM173B

Files

EBSD (1)

Settings

Date:

10/2/2023

Scan Number:

Scan1

Sample Cut Direction:

Cross-section

Sample Orientation:

ED Out of plane

Scan Width:

500 µm

Scan Height:

384 µm

Step size:

1 µm

Voltage:

30 kV

Beam Intensity:

20

Location:

DOW Allison Lab

Equipment:

Tescan Mira3

Operator:

Qianying Shi

Equipment:

Tescan Mira3

Operator:

Qianying Shi

Measurements

Alloy:

Mg1Y

Composition Y Content:

1 wt%

Casting Billet:

N2134

Extrusion Bar Number:

UM173B

Files

Heat Treatment (1)

Settings

Complete Date:

8/25/2023

Equipment:

Oil Bath

Temperature:

177 ℃

Time:

2 month hr

HT Atmosphere:

Air

Location:

DOW Allison Lab

Cooling Method:

Water Quench

Operator:

Qianying Shi

Measurements

Alloy:

Mg1Y

Composition Y Content:

1 wt%

Casting Billet:

N2134

Extrusion Bar Number:

UM173B

TEM (3)

Settings

Date:

10/23/2023

Foil Making Method:

FIB Lift-out

Equipment:

Talos

Stage:

Double Tilt

Voltage:

200 kV

Mode:

EDS

Spot Size:

6

Gun Length:

4

Camera Length:

98 cm

EDS Map Magnification:

380

EDS Map Width:

50 nm

EDS Map Height:

100 nm

EDS Map Dwell Time:

50 us

EDS Map Binning:

512 x 512

Location:

MC2

Operator:

Qianying Shi

Measurements

Alloy:

Mg1Y

Composition Y Content:

1 wt%

Casting Billet:

N2134

Extrusion Bar Number:

UM173B

Files

See 128 more files......

TEM Foil Fabrication (1)

Settings

Date:

10/9/2023

Method:

FIB Lift-out

Location:

MC2

Liftout Cutting Geometry:

Plan-view

Equipment:

Helios 650 Nanolab + Helios G4 PFIB UXe

FIB Source:

Ga + Xe

Final Thinning Condition:

Xe PFIB

Measurements

Alloy:

Mg1Y

Composition Y Content:

1 wt%

Casting Billet:

N2134

Extrusion Bar Number:

UM173B