Sample: ZX30_10pct_TD200_AS-DEF

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78862
EBSD (2)
Settings
Scan date:
5/13/24
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Width:
300 µm
Scan Height:
250 µm
Scan Height:
400 µm
Step size:
0.15 µm
Step size:
1 µm
frames per second:
66 fps
EBSD Camera Binning:
1 x 1
Background setting:
standard
Grid type:
hexagonal
Grid type:
square
Final Polishing Step:
fumed Si
CI>0.1 after rescan:
0.835
CI>0.1 after rescan:
0.854
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.6679
% points with CI>0.1:
0.681
Alloy:
ZX30
Average dislocation density:
1.4*10^14
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
1.5 %
Total Fraction Less than 1º:
0.2 %
Composition Ca content:
0.096 wt%
Number of grains:
485
Number of grains:
170
Average Diameter:
19 µm
Average Diameter:
17 µm
Files
Gleeble (1)
Settings
Test Date:
4/26/24
Testing Mode:
PSC
Initial height or thickness:
9.96 mm
Initial width:
15 mm
Initial length:
19.97 mm
Final height or thickness:
9.22 mm
Final length:
20.55 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200 ºC
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.6679
% points with CI>0.1:
0.681
Alloy:
ZX30
Average dislocation density:
1.4*10^14
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
1.5 %
Total Fraction Less than 1º:
0.2 %
Composition Ca content:
0.096 wt%
Number of grains:
170
Number of grains:
485
Average Diameter:
17 µm
Average Diameter:
19 µm
Files
GND Calculation (2)
Measurements
% points with CI>0.1:
0.6679
% points with CI>0.1:
0.681
Alloy:
ZX30
Average dislocation density:
1.4*10^14
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
1.5 %
Total Fraction Less than 1º:
0.2 %
Composition Ca content:
0.096 wt%
Number of grains:
170
Number of grains:
485
Average Diameter:
19 µm
Average Diameter:
17 µm
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.681
% points with CI>0.1:
0.6679
Alloy:
ZX30
Average dislocation density:
1.4*10^14
Unloaded strain:
7%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
1.5 %
Total Fraction Less than 1º:
0.2 %
Composition Ca content:
0.096 wt%
Number of grains:
485
Number of grains:
170
Average Diameter:
17 µm
Average Diameter:
19 µm