Sample: ZX30_10pct_TD200_TA350_0s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78863
EBSD (5)
Settings
Scan date:
5/13/24
Scan date:
5/16/24
Sample orientation vertical direction:
RD
SEM view field width:
550 µm
Scan date:
3/7/25
SEM view field width:
200 µm
SEM view field width:
550 µm
Scan Width:
400 µm
Scan Width:
80 µm
Scan Width:
400 µm
Scan Height:
400 µm
Scan Height:
80 µm
Scan Height:
400 µm
Step size:
1 µm
Step size:
0.25 µm
Step size:
1 µm
frames per second:
66 fps
EBSD Camera Binning:
1 x 1
frames per second:
69 fps
EBSD Camera Binning:
1 x 1
Background setting:
enhanced
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Grid type:
hex
Final Polishing Step:
Master Polish
Final Polishing Step:
fumed Si
Voltage:
30 kV
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.823
% points with CI>0.1:
0.8469
% points with CI>0.1:
0.81
% points with CI>0.1:
0.843
% points with CI>0.1:
0.83
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
10.8 %
Total Fraction Less than 1º:
12.5 %
Total Fraction Less than 1º:
6 %
Total Fraction Less than 1º:
7.7 %
Total Fraction Less than 1º:
9.8 %
Composition Ca content:
0.096 wt%
Number of grains:
360
Number of grains:
405
Number of grains:
404
Number of grains:
358
Average Diameter:
17 µm
Average Diameter:
18 µm
Average Diameter:
19 µm
Average Diameter:
17.7 µm
Twin fraction:
0.056
Files
Gleeble (1)
Settings
Test Date:
4/26/24
Testing Mode:
PSC
Initial height or thickness:
9.96 mm
Initial width:
14.95 mm
Initial length:
19.95 mm
Final height or thickness:
9.03 mm
Final length:
20.6 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
0 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.8469
% points with CI>0.1:
0.843
% points with CI>0.1:
0.81
% points with CI>0.1:
0.823
% points with CI>0.1:
0.83
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
7.7 %
Total Fraction Less than 1º:
10.8 %
Total Fraction Less than 1º:
12.5 %
Total Fraction Less than 1º:
6 %
Total Fraction Less than 1º:
9.8 %
Composition Ca content:
0.096 wt%
Number of grains:
404
Number of grains:
358
Number of grains:
360
Number of grains:
405
Average Diameter:
17.7 µm
Average Diameter:
19 µm
Average Diameter:
18 µm
Average Diameter:
17 µm
Twin fraction:
0.056
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.81
% points with CI>0.1:
0.83
% points with CI>0.1:
0.843
% points with CI>0.1:
0.8469
% points with CI>0.1:
0.823
Alloy:
ZX30
Unloaded strain:
9%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
9.8 %
Total Fraction Less than 1º:
10.8 %
Total Fraction Less than 1º:
7.7 %
Total Fraction Less than 1º:
12.5 %
Total Fraction Less than 1º:
6 %
Composition Ca content:
0.096 wt%
Number of grains:
358
Number of grains:
404
Number of grains:
360
Number of grains:
405
Average Diameter:
17 µm
Average Diameter:
18 µm
Average Diameter:
17.7 µm
Average Diameter:
19 µm
Twin fraction:
0.056