Sample: ZX30_10pct_TD200_TA350_120s

Ungroup Processes

Last Updated: 2 weeks ago Owner: Tracy Berman ID: 78864
EBSD (3)
Settings
Sample orientation vertical direction:
RD
Scan date:
5/20/24
Scan date:
5/14/24
Scan date:
3/7/25
SEM view field width:
550 µm
Scan Width:
400 µm
SEM view field width:
550 µm
Scan Height:
400 µm
Scan Width:
400 µm
Scan Height:
400 µm
Step size:
1 µm
Step size:
1 µm
frames per second:
66 fps
frames per second:
100 fps
EBSD Camera Binning:
1 x 1
EBSD Camera Binning:
1 x 1
Background setting:
standard
Background setting:
enhanced
Background setting:
standard
Grid type:
hexagonal
Final Polishing Step:
fumed Si
Grid type:
hex
Voltage:
30 kV
Final Polishing Step:
fumed Si
Beam Intensity or current:
20
Voltage:
30 kV
Beam Intensity or current:
20
Measurements
% points with CI>0.1:
0.91
% points with CI>0.1:
0.831
Alloy:
ZX30
Unloaded strain:
10%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
83.1 %
Total Fraction Less than 1º:
61 %
Total Fraction Less than 1º:
41.5 %
Composition Ca content:
0.096 wt%
Number of grains:
254
Number of grains:
284
Number of grains:
304
Average Diameter:
25 µm
Average Diameter:
23.4 µm
Average Diameter:
22 µm
Twin fraction:
0.002
Files
Gleeble (1)
Settings
Test Date:
5/8/24
Testing Mode:
PSC
Initial height or thickness:
9.97 mm
Initial width:
14.98 mm
Initial length:
19.97 mm
Final height or thickness:
8.99 mm
Final length:
20.65 mm
Pre-deformation soak Temp:
200 ºC
Deformations:
1
Initial Strain Rate:
0.5 /s
Strain Per pass:
0.1
Stage One - Temp during Deformations:
200 ºC
Post-deformation Soak Temp:
350 ºC
Post-deformation Soak Time:
120 s
Quench Duration:
45 s
Rate to Temp:
5 ºC/s
Program Strain Type:
TRUE
Pre-deformation Soak Time:
600 s
Specimen orientation:
CD || ED
Measurements
% points with CI>0.1:
0.91
% points with CI>0.1:
0.831
Alloy:
ZX30
Unloaded strain:
10%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
41.5 %
Total Fraction Less than 1º:
61 %
Total Fraction Less than 1º:
83.1 %
Composition Ca content:
0.096 wt%
Number of grains:
254
Number of grains:
284
Number of grains:
304
Average Diameter:
23.4 µm
Average Diameter:
25 µm
Average Diameter:
22 µm
Twin fraction:
0.002
Files
Receive Samples (1)
Settings
Receipt Date:
4/28/22
Source:
CanMET
Solution treatment time:
1 hr
Solution treatment Temp:
325 ºC
Measurements
% points with CI>0.1:
0.831
% points with CI>0.1:
0.91
Alloy:
ZX30
Unloaded strain:
10%
Composition Zn content:
3.03 wt%
Total Fraction Less than 1º:
41.5 %
Total Fraction Less than 1º:
83.1 %
Total Fraction Less than 1º:
61 %
Composition Ca content:
0.096 wt%
Number of grains:
304
Number of grains:
254
Number of grains:
284
Average Diameter:
23.4 µm
Average Diameter:
22 µm
Average Diameter:
25 µm
Twin fraction:
0.002
Files